Gd/Sm-Pr Co-Doped Ceria: A First Report of the Precipitation Method Effect on Flash Sintering.

In this work, ceria-based ceramics with the composition Gd0.14Pr0.06Ce0.8O2-δ and Sm0.14Pr0.06Ce0.8O2-δ, were synthesized by a simple co-precipitation process using either ammonium carbonate or ammonia solution as a precipitating agent. After the calcination, all of the produced samples were constituted by fluorite-structured ceria only, thus showing that both dopant and co-dopant cations were dissolved in the fluorite lattice. The ceria-based nanopowders were uniaxially compacted and consequently flash-sintered using different electrical cycles (including current-ramps). Different results were obtained as a function of both the adopted precipitating agent and the applied electrical cycle. In particular, highly densified products were obtained using current-ramps instead of "traditional" flash treatments (with the power source switching from voltage to current control at the flash event). Moreover, the powders that were synthesized using ammonia solution exhibited a low tendency to hotspot formation, whereas the materials obtained using carbonates as the precipitating agent were highly inhomogeneous. This points out for the first time the unexpected relevance of the precipitating agent (and of the powder shape/degree of agglomeration) for the flash sintering behavior.

Investigation of Electrochemical, Optical and Thermal Effects during Flash Sintering of 8YSZ.

This paper reports the electrochemical, optical and thermal effects occurring during flash sintering of 8 mol % yttria-stabilized zirconia (8YSZ). In-situ observations of polycrystalline and single crystal specimens revealed electrochemical blackening/darkening during an incubation period prior to flash sintering. The phenomenon is induced by cathodic partial reduction under DC fields. When using a low frequency AC field (0.1⁻10 Hz) the blackening is reversible, following the imposed polarity switching. Thermal imaging combined with sample colour changes and electrical conductivity mapping give a complete picture of the multi-physical phenomena occurring during each stage of the flash sintering event. The partial reduction at the cathode causes a modification of the electrical properties in the sample and the blackened regions, which are close to the cathode, are more conductive than the remainder of the sample. The asymmetrical nature of the electrochemical reactions follows the field polarity and causes an asymmetry in the temperature between the anode and cathode, with the positive electrode tending to overheat. It is also observed that the phenomena are influenced by the quality of the electrical contacts and by the atmosphere used.