ABSTRACT
The product of ozonolysis, glycero-(9,10-trioxolane)-trioleate (ozonide of oleic acid triglyceride, [OTOA]), was incorporated into polylactic acid/polycaprolactone (PLA/PCL) blend films in the amount of 1, 5, 10, 20, 30 and 40% w/w. The morphological, mechanical, thermal and antibacterial properties of the biodegradable PLA/PCL films after the OTOA addition were studied. According to DSC and XRD data, the degree of crystallinity of the PLA/PCL + OTOA films showed a general decreasing trend with an increase in OTOA content. Thus, a significant decrease from 34.0% for the reference PLA/PCL film to 15.7% for the PLA/PCL + 40% OTOA film was established using DSC. Observed results could be explained by the plasticizing effect of OTOA. On the other hand, the PLA/PCL film with 20% OTOA does not follow this trend, showing an increase in crystallinity both via DSC (20.3%) and XRD (34.6%). OTOA molecules, acting as a plasticizer, reduce the entropic barrier for nuclei formation, leading to large number of PLA spherulites in the plasticized PLA/PCL matrix. In addition, OTOA molecules could decrease the local melt viscosity at the vicinity of the growing lamellae, leading to faster crystal growth. Morphological analysis showed that the structure of the films with an OTOA concentration above 20% drastically changed. Specifically, an interface between the PLA/PCL matrix and OTOA was formed, thereby forming a capsule with the embedded antibacterial agent. The moisture permeability of the resulting PLA/PCL + OTOA films decreased due to the formation of uniformly distributed hydrophobic amorphous zones that prevented water penetration. This architecture affects the tensile characteristics of the films: strength decreases to 5.6 MPa, elastic modulus E by 40%. The behavior of film elasticity is associated with the redistribution of amorphous regions in the matrix. Additionally, PLA/PCL + OTOA films with 20, 30 and 40% of OTOA showed good antibacterial properties on Pseudomonas aeruginosa, Raoultella terrigena (Klebsiella terrigena) and Agrobacterium tumefaciens, making the developed films potentially promising materials for wound-dressing applications.
ABSTRACT
Glycero-(9,10-trioxolane)-trioleate (ozonide of oleic acid triglyceride, OTOA) was introduced into polylactic acid (PLA) films in amounts of 5, 10, 30, 50, and 70% w/w. The morphological, mechanical, thermal, and water absorption properties of PLA films after the OTOA addition were studied. The morphological analysis of the films showed that the addition of OTOA increased the diameter of PLA spherulites and, as a consequence, increased the proportion of amorphous regions in PLA films. A study of the thermodynamic properties of PLA films by differential scanning calorimetry (DSC) demonstrated a decrease in the glass transition temperature of the films with an increase in the OTOA content. According to DSC and XRD data, the degree of crystallinity of the PLA films showed a tendency to decrease with an increase in the OTOA content in the films, which could be accounted for the plasticizing effect of OTOA. The PLA film with 10% OTOA content was characterized by good smoothness, hydrophobicity, and optimal mechanical properties. Thus, while maintaining high tensile strength of 21 MPa, PLA film with 10% OTOA showed increased elasticity with 26% relative elongation at break, as compared to the 2.7% relative elongation for pristine PLA material. In addition, DMA method showed that PLA film with 10% OTOA exhibits increased strength characteristics in the dynamic load mode. The resulting film materials based on optimized PLA/OTOA compositions could be used in various packaging and biomedical applications.
ABSTRACT
This work addresses hydrophilization of hydrophobic mesoporous membranes based on high-density polyethylene (HDPE) via ozonation. Mesoporous HDPE membranes were prepared by intercrystallite environmental crazing. Porosity was 50%, and pore dimensions were below 10 nm. Contact angle of mesoporous membranes increases from 96° (pristine HDPE) to 120° due to the formation of nano/microscale surface relief and enhanced surface roughness. The membranes are impermeable to water (water entry threshold is 250 bar). The prepared membranes were exposed to ozonation and showed a high ozone uptake. After ozonation, the membranes were studied by different physicochemical methods, including DSC, AFM, FTIR spectroscopy, etc. Due to ozonation, wettability of the membranes was improved: their contact angle decreased from 120° down to 60°, and they became permeable to water. AFM micrographs revealed a marked smoothening of the surface relief, and the FTIR spectra indicated the development of new functionalities due to ozonolysis. Both factors contribute to hydrophilization and water permeability of the ozonated HDPE membranes. Hence, ozonation was proved to be a facile and efficient instrument for surface modification of hydrophobic mesoporous HDPE membranes and can also provide their efficient sterilization for biomedical purposes and water treatment.
ABSTRACT
Biocompatible glycero (9,10-trioxolane) trioleate (ozonide of oleic acid triglyceride, OTOA) was incorporated into polylactic acid (PLA) fibers by electrospinning and nonwoven PLA mats with 1%, 3% and 5% OTOA content. The morphological, mechanical, thermal and water sorption properties of electrospun PLA mats after the addition of OTOA were studied. A morphological analysis showed that the addition of OTOA increased the average fiber diameter and induced the formation of pores on the fiber surface, leading to an increase in the specific surface area for OTOA-modified PLA fibrous mats. PLA fiber mats with 3% OTOA content were characterized by a highly porous surface morphology, an increased specific surface area and high-water sorption. Differential scanning calorimetry (DSC) was used to analyze the thermal properties of the fibrous PLA mats. The glass transition temperatures of the fibers from the PLA-OTOA composites decreased as the OTOA content increased, which was attributed to the plasticizing effect of OTOA. DSC results showed that OTOA aided the PLA amorphization process, thus reducing the crystallinity of the obtained nonwoven PLA-OTOA materials. An analysis of the mechanical properties showed that the tensile strength of electrospun PLA mats was improved by the addition of OTOA. Additionally, fibrous PLA mats with 3% OTOA content showed increased elasticity compared to the pristine PLA material. The obtained porous PLA electrospun fibers with the optimal 3% OTOA content have the potential for various biomedical applications such as drug delivery and in tissue engineering.