ABSTRACT
The aim of the presented work is to combine luminescent porous silicon (PSi) with a ferromagnetic metal (Ni) to modify on the one hand the photoluminescence by the presence of metal deposits and on the other hand to influence the optical properties by an external magnetic field. The optical properties are investigated especially with respect to the wavelength-shift of the photoluminescence due to the metal filling. With increasing metal deposits within PSi the photoluminescence peak is blue-shifted and furthermore an increase of the intensity is observed. Photoluminescence spectra of bare PSi show a maximum around 620 nm whereas in the case of Ni filled samples the peak is blue-shifted to around 580 nm for a deposition time of 15 min. Field dependent magnetic measurements performed with an applied field parallel and perpendicular to the surface, respectively, show a magnetic anisotropy which is in agreement with a thin film. This film-like behavior is caused by the interconnected Ni structures due to the branched porous silicon morphology. The coercivity increases with increasing metal deposition from about 150 Oe to about 450 Oe and also the magnetic anisotropy is enhanced with the growth of metal deposits. Within this work the influence of the magnetic metal filling on the optical properties and the magnetic characterization of the nanocomposites are discussed. The presented systems give not only rise to optoelectronics applications but also to magneto optical integrated devices.
ABSTRACT
After organic photovoltaic (OPV) cells achieved efficiency of more than 10%, the control of stability and degradation mechanisms of solar cells became a prominent task. The increase of device efficiency due to incorporation of a hole-transport layer (HTL) in bulk-heterojunction solar cells has been extensively reported. However, the most widely used HTL material, poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS), is frequently suspected to be the dominating source for device instability under environmental conditions. Thereby, effects like photooxidation and electrode corrosion are often reported to shorten device lifetime. However, often in environmental device studies, the source of degradation, whether being from the HTL, the active layer, or the metal cathode is rather difficult to distinguish because the external diffusion of oxygen and water affects all components. In this study, different HTLs, namely, those prepared from traditional PEDOT:PSS and also two types of molybdenum trioxide (MoO3) are exposed to different environments, such as oxygen, light, or humidity, prior to device finalization under inert conditions. This allows investigating any effects within the HTL and from reactions at its interface to the indium tin oxide electrode or the active layer. The surface and bulk chemistry of the exposed HTL has been monitored and discussed in context to the observed device physics, dynamic charge transport, and spatial performance homogeneity of the corresponding OPV device. The results show that merely humidity exposure of the HTL leads to decreased device performance for PEDOT:PSS, but also for one type of the tested MoO3. The losses are related to the amount of absorbed water in the HTL, inducing loss of active area in terms of interfacial contact. The device with PEDOT:PSS HTL after humid air exposure showed seriously decreased photocurrent by microdelamination of swelling/shrinkage of the hygroscopic layer. The colloidal MoO3 with water-based precursor solution presents slight decay of solar cell performance, also here caused by swelling/shrinking reaction, but by a combination of in-plane particle contact and resistance scaling with particle expansion. However, the device with quasi-continuous and alcohol-based MoO3 showed unharmed stable electrical performance.
ABSTRACT
Electrochemically deposited magnetic nanostructures arranged in a three-dimensional system are investigated with respect to their cross-talk between each other. The nanostructures are embedded in porous silicon templates with different morphologies which means pores offering dendritic growth of different strengths. An increase of the uniformity of the pores is concomitant with an increase of the smoothness of the metal deposits which strongly influences the magnetic behavior of the system. Less dendritic structures lead to an increase of the coercivity of the nanocomposite which reveals less cross-talk between the metal deposits due to a modification of the stray fields. The system allows in a cheap and simple way to tune the magnetic interactions of magnetic nanostructures in a three-dimensional arrangement. PACS: 81.05.Rm; 81.07.Gf; 75.75.-c.
ABSTRACT
A variety of methods for the investigation and 3D representation of the inner structure of materials has been developed. In this paper, techniques based on slice and view using scanning microscopy for imaging are presented and compared. Three different methods of serial sectioning combined with either scanning electron or scanning ion microscopy or atomic force microscopy (AFM) were placed under scrutiny: serial block-face scanning electron microscopy, which facilitates an ultramicrotome built into the chamber of a variable pressure scanning electron microscope; three-dimensional (3D) AFM, which combines an (cryo-) ultramicrotome with an atomic force microscope, and 3D FIB, which delivers results by slicing with a focused ion beam. These three methods complement one another in many respects, e.g., in the type of materials that can be investigated, the resolution that can be obtained and the information that can be extracted from 3D reconstructions. A detailed review is given about preparation, the slice and view process itself, and the limitations of the methods and possible artifacts. Applications for each technique are also provided.
ABSTRACT
In the frame of this work, the aim was to create a superparamagnetic nanocomposite system with a maximized magnetic moment when magnetized by an external field and a blocking temperature far below room temperature. For this purpose, iron oxide nanoparticles of 3.8-, 5- and 8-nm size have been infiltrated into the pores of porous silicon. To fabricate tailored magnetic properties of the system, the particle size and the magnetic interactions among the particles play a crucial role. Different concentrations of the particles dispersed in hexane have been used for the infiltration to vary the blocking temperature TB, which indicates the transition between the superparamagnetic behavior and blocked state. TB is not only dependent on the particle size but also on the magnetic interactions between them, which can be varied by the particle-particle distance. Thus, a modification of the pore loading on the one hand and of the porous silicon morphology on the other hand results in a composite material with a desired blocking temperature. Because both materials, the mesoporous silicon matrices as well as the Fe3O4 nanoparticles, offer low toxicity, the system is a promising candidate for biomedical applications.
ABSTRACT
Ferromagnetic nanostructures have been electrodeposited within the pores of porous silicon templates with average pore diameters between 25 and 60 nm. In this diameter regime, the pore formation in general is accompanied by dendritic growth resulting in rough pore walls, which involves metal deposits also offering a branched structure. These side branches influence the magnetic properties of the composite system not only due to modified and peculiar stray fields but also because of a reduced interpore spacing by the approaching of adjacent side pores. To improve the morphology of the porous silicon structures, a magnetic field up to 8 T has been applied during the formation process. The magnetic field etching results in smaller pore diameters with less dendritic side pores. Deposition of a ferromagnetic metal within these templates leads to less branched nanostructures and, thus, to an enhancement of the coercivity of the system and also to a significantly increased magnetic anisotropy. So magnetic field-assisted etching is an appropriate tool to improve the structure of the template concerning the decrease of the dendritic pore growth and to advance the magnetic properties of the composite material.
ABSTRACT
Reinvestigation of the Lewis acid catalyzed rearrangement of some open-chain permethyloligosilanes with the Al(Fe)Cl(3) catalyst system exhibited several cases of additional reactivity: namely, a fragmentation/cyclization reaction. Introduction of (trimethylsilyl)methyl substituents into the oligosilane substrates strongly facilitated this reaction, yielding cyclic or bicyclic carbacyclosilanes. Investigations concerning the composition of the catalyst system indicated that the incorporation of about 0.1% FeCl(3) into the AlCl(3) lattice provided an effective catalyst.
ABSTRACT
In this study, to assess the influence of the temperature on the ion beam degradation, irradiation experiments on organic semiconductor materials were performed for both cryogenic and room temperature conditions. Thin P3HT films on silicon substrates were exposed to increasing ion doses in dual beam FIB. The degradation behaviour by means of a decrease in the C[double bond, length as m-dash]C band which corresponds to a loss of conjugation was investigated by means of Raman spectroscopy. In addition, atomic force microscopy (AFM) and Kelvin probe force microscopy (KPFM) were used for a characterization of morphology and surface potential which provide information on temperature and ion dose dependent degradation behaviour.