ABSTRACT
Transparent fluorotellurite glasses were prepared by melt-quenching in the ternary system TeO2-Nb2O5-PbF2. The synthesis conditions were adjusted to minimize fluorine loss monitored as HF release. It was found that 10 mol% of Nb2O5 is the optimum content for PbF2 incorporation up to 35 mol% in the tellurite matrix without loss of glass forming ability. Such glass compositions exhibit a wide optical window from 380 nm to about 6 µm. Crystallization properties were carefully investigated by thermal analysis and compositions with higher PbF2 contents exhibit preferential precipitation of lead oxyfluoride Pb2OF2 at lower temperatures. The lead oxyfluoride crystallization mechanism is also governed by a volume nucleation, barely reported in tellurite glasses. Eu3+ doping of these glass compositions also promotes a more efficient nucleation step under suitable heat-treatments, resulting in transparent Eu3+-doped glass-ceramics whereas undoped glass-ceramics are translucent. Finally, Eu3+ spectroscopy pointed out a progressive, more symmetric surrounding around the rare earth ions with increasing PbF2 contents as well as higher quantum efficiencies. These new fluorotellurite glass compositions are promising as luminescent hosts working in the middle infrared.
ABSTRACT
In this work, vitreous samples were prepared in the binary system (100 - x)NaPO3-xMO3 with M = Mo and W and x varying from 10 to 60. The transmittance properties in the UV, visible, and near-infrared were monitored as a function of MO3 concentration. In both cases, an increase in the amount of transition metal results in an intense and broad absorption band in the visible and near-infrared attributed to metal reduction under synthesis conditions. It was shown that this large absorption can be partially or totally removed using specific oxidizing agents or by improving synthesis parameters such as melting temperature or cooling rate of the melt. In addition, structural investigations by Raman and X-ray absorption spectroscopy suggest that reduction only occurs when the metal cation is in octahedral geometry and that the transmittance improvement is not related with any structural changes. These results were explained in terms of thermodynamic equilibrium of redox species in the melt and allowed to obtain for the first time transparent and chemically stable glasses containing high concentrations of MO3 with transition metals in octahedral geometry inside the glass network.
Subject(s)
Molybdenum/chemistry , Phosphates/chemistry , Tungsten/chemistry , Oxidation-Reduction , SpectrophotometryABSTRACT
Vitreous samples were prepared in the (100 - x)% NaPO(3)-x% MoO(3) (0
ABSTRACT
In this work, we present a new photochromic tungstate based glass which have both absorption coefficient and refractive index modified under laser exposure. The photosensitive effect is superficial under ultraviolet (UV) irradiation but occurs in the entire volume of the glass under visible irradiation. The effect can be obtained in any specific point inside the volume using an infrared femtosecond laser. In addition, the photosensitive phenomenon can be erased by specific heat treatment. This glass can be useful to substitute actual data storage supports and is a promising material for 3-dimensional (3D) and holographic optical storage.