The interface between chloroaluminum phthalocyanine and titanium dioxide: the influence of surface defects and substrate termination.

Interface properties of chloroaluminum(iii) phthalocyanine (AlClPc) on two different rutile titanium dioxide (TiO2) single crystal surfaces ((100) and (001)) have been studied using X-ray and ultraviolet photoemission spectroscopy (XPS and UPS). It is shown that the strength of the interaction clearly depends on the substrate termination and preparation. Generally, the (001) surface is more reactive compared to the (100) surface. The most important interaction channel involves the nitrogen atoms of the phthalocyanine macrocycle. An exposure to oxygen during the annealing steps of the preparation procedure allows diminishing the extent of interaction of nitrogen with titanium dioxide. The work function of AlClPc/TiO2 is rather independent of the substrate, indicating a pinning regime at all interfaces, where the HOMO of the molecule is aligned at the maximum of the defect states of the substrate.

FePc and FePcF16 on Rutile TiO2(110) and (100): Influence of the Substrate Preparation on the Interaction Strength.

Interface properties of iron phthalocyanine (FePc) and perfluorinated iron phthalocyanine (FePcF16) on rutile TiO2(100) and TiO2(110) surfaces were studied using X-ray photoemission spectroscopy (XPS), X-ray absorption spectroscopy (XAS), and low-energy electron diffraction (LEED). It is demonstrated that the interaction strength at the interfaces is considerably affected by the detailed preparation procedure. Weak interactions were observed for all studied interfaces between FePc or FePcF16 and rutile, as long as the substrate was exposed to oxygen during the annealing steps of the preparation procedure. The absence of oxygen in the last annealing step only had almost no influence on interface properties. In contrast, repeated substrate cleaning cycles performed in the absence of oxygen resulted in a more reactive, defect-rich substrate surface. On such reactive surfaces, stronger interactions were observed, including the cleavage of some C-F bonds of FePcF16.

Communication: Influence of graphene interlayers on the interaction between cobalt phthalocyanine and Ni(111).

The influence of graphene interlayers on electronic interface properties of cobalt phthalocyanine on Ni(111) is studied using both photoemission and X-ray absorption spectroscopy. A charge transfer associated with a redistribution of the d-electrons at the Co-atom of the phthalocyanine occurs at the interface to Ni(111). Even a graphene buffer layer cannot prevent the charge transfer at the interface to Ni(111); however, the detailed electronic situation is different.