ABSTRACT
The article presents research results on the possibility of shaping the structure and properties of Co-Cr-W-C-Ti alloys (type Stellite 6) using laser cladding technology. Cobalt-based alloys are used in several industries because they are characterized by high erosion, abrasion, and corrosion resistance, retaining these properties at high temperatures. To further increase erosion resistance, it seems appropriate to reinforce material by in situ synthesis of hard phases. Among the transition metal carbides (TMCs), titanium carbide is one of the hardest and can have a positive effect on the extension of the lifetime of components made from cobalt-based alloys. In this article, concentration of C, W, and Ti due to the possibility of in situ synthesis of titanium carbides was subjected to detailed analysis. The provided research includes macrostructure and microstructure analysis, X-ray diffraction (XRD), microhardness, and penetrant tests. It was found that the optimal concentrations of Ti and C in the Co-Cr-W-C alloy allow the formation of titanium carbides, which significantly improves erosion resistance for low impact angles. Depending on the concentrations of titanium, carbon, and tungsten in the molten metal pool, it is possible to shape the alloy structure by influencing to morphology and size of the reinforcing phase in the form of the complex carbide (Ti,W)C.
ABSTRACT
This article presents production results concerning metal matrix composite-coatings made using the laser-cladding technology. The enhancement of the wear resistance of the material surface is the one of the main goals accompanying the manufacturing of composite coatings. Nickel-based superalloys are used in several industries because they are characterized by a number of desirable properties including high tensile and fatigue strength as well as resistance to high-temperature corrosion in aggressive environments. One of the most interesting materials from the group of superalloys is Inconel 625, used as a matrix material in tests discussed in this article. However, nickel-based superalloys are also characterized by an insufficient wear resistance of the surface, therefore, in relation to the tests discussed in this article, Inconel 625-based composite coatings were reinforced by adding 10%, 20% and 40% of titanium carbide particles. The addition of hard phases, i.e., TiC, WC or SiC particles can have a positive effect on the erosion resistance of cladded specimens. The aim of the experiment was to determine the impact of the titanium carbide content on the structure of the alloy and its resistance to corrosive wear, enabling the extension of the service life of Inconel 625/TiC composite coatings. The investigation included microhardness tests, corrosion resistance analysis, penetrant tests, macrostructure and microstructure analyses and X-ray diffraction (XRD) tests. The TiC particles increased the hardness of the coatings and, in general, had a negative impact on the corrosion resistance of pure Inconel 625 coatings. However, the increased homogeneity of composite coatings translated into the improvement of corrosion resistance.
ABSTRACT
The article presents research in the field of laser cladding of metal-matrix composite (MMC) coatings. Nickel-based superalloys show attractive properties including high tensile strength, fatigue resistance, high-temperature corrosion resistance and toughness, which makes them widely used in the industry. Due to the insufficient wear resistance of nickel-based superalloys, many scientists are investigating the possibility of producing nickel-based superalloys matrix composites. For this study, the powder mixtures of Inconel 625 superalloy with 10, 20 and 40 vol.% of TiC particles were used to produce MMC coatings by laser cladding. The titanium carbides were chosen as reinforcing material due to high thermal stability and hardness. The multi-run coatings were tested using penetrant testing, macroscopic and microscopic observations, microhardness measurements and solid particle erosive test according to ASTM G76-04 standard. The TiC particles partially dissolved in the structure during the laser cladding process, which resulted in titanium and carbon enrichment of the matrix and the occurrence of precipitates formation in the structure. The process parameters and coatings chemical composition variation had an influence on coatings average hardness and erosion rates.