ABSTRACT
The possibility of using thermoplastic polymers in photopolymer compositions for SLA and DLP is discussed in this article. The diffusion and mutual solubility of uncured systems based on tert-butyl acrylate (tBA) and ethylene-vinyl acetate copolymers (EVA) or low-density polyethylene (LDPE) were studied. The solubility and diffusion of tBA with EVA containing 7, 20, and 40 wt.% vinyl acetate (VA) and with LDPE in the temperature range 20-75 °C were studied by optical micro-interferometry method. Phase diagrams of LDPE-tBA, EVA-7-tBA, and EVA-20-tBA systems were obtained. It is shown that the compositions are characterized by the phase-state diagrams of amorphous separation with the upper critical solution temperature (UCST). The concentration dependences of the interdiffusion coefficients as well as dependences of the self-diffusion coefficients on VA content and on temperature were plotted. The activation energy of self-diffusion of EVA and LDPE was calculated. It was shown that the most promising tBA modifier is EVA-40, which is completely soluble at all studied temperature ranges. The obtained data on the mixing of the initial components is valuable for further studies of the processes of structure formation during photocuring of compositions, regulation of the phase structure and, as a consequence, the performance characteristics of the 3D printable materials.
ABSTRACT
The development of universal finishing compositions for fibers of various natures is an urgent task for polymer composite materials science. The developed finishes can be used for the fiber reinforcement of polymer matrices with a wide range of surface free energy characteristics. Epoxy systems modified with diaminesilane in a wide concentration range were examined by optical interferometry, FTIR spectroscopy, DSC and the sessile drop technique. It was shown that the partial curing of epoxy resin by diaminesilane at room temperature under an inert atmosphere, followed by contact with air, leads to a significant increase of the surface free energy of the system. Varying the concentration of diaminesilane allows us to effectively regulate the surface free energy of the composition. This makes it possible to use fibers finished with epoxyaminosilane compositions in composite materials based on a various thermosetting and thermoplastic binders with a surface tension of up to 75 mJ/m2.
ABSTRACT
The mutual solubility of epoxy oligomer with polysulfone (PSU) and polyethersulfone (PES) was studied by optical interferometry. Additionally, phase diagrams (PDs) were plotted and their evolution during the curing process was shown. The phase structures of modified hardened systems, as well as their tensile strengths, elastic moduli, and crack resistance, have been studied by scanning electron microscopy and physico-mechanical techniques. The effect of initial components' mutual solubility on the phase structure and, subsequently, on the physico-mechanical properties of the composite material is shown. Differences in the structure and properties of the cured modified compositions depending on the type of PD (with Upper Critical Solution Temperature (UCST) for PSU and Lower Critical Solution Temperature (LCST) for PES) of the initial components are shown.