ABSTRACT
Charge separation and extraction dynamics were investigated in high-performance bulk heterojunction solar cells made from the polymer PTB7 and the soluble fullerene PC71BM on a broad time scale from subpicosecond to microseconds using ultrafast optical probing of carrier drift and the integral-mode photocurrent measurements. We show that the short circuit current is determined by the separation of charge pairs into free carriers, which is strongly influenced by blend composition. This separation is found to be efficient in fullerene-rich blends where a high electron mobility of >0.1 cm2 V-1 s-1 is observed in the first 10 ps after excitation. Morphology optimization using the solvent additive 1,8-diiodooctane (DIO) doubles the charge pair separation efficiency and the short-circuit current. Carrier extraction at low internal electric field is slightly faster from the cells prepared with DIO, which can reduce recombination losses and enhance a fill factor.
ABSTRACT
In this paper we studied carrier drift dynamics in APFO3:PC61BM solar cells of varied stoichiometry (2:1, 1:1, and 1:4 APFO3:PC61BM) over a wide time range, from subpicoseconds to microseconds with a combination of ultrafast optical electric field probing and conventional transient integrated photocurrent techniques. Carrier drift and extraction dynamics are strongly stoichiometry dependent: the speed of electron or hole drift increases with higher concentration of PC61BM or polymer, respectively. The electron extraction from a sample with 80% PC61BM takes place during hundreds of picoseconds, but slows down to sub-microseconds in a sample with 33% PC61BM. The hole extraction is less stoichiometry dependent: it varies form sub-nanoseconds to tens of nanoseconds when the PC61BM concentration changes from 33% to 80%. The electron extraction rate correlates with the conversion efficiency of solar cells, leading to the conclusion that fast electron motion is essential for efficient charge carrier separation preventing their geminate recombination.