ABSTRACT
The design and manufacture of innovative multifunctional materials possessing superior characteristics, quality and standards, rigorously required for future development of existing or emerging advanced technologies, is of great importance. These materials should have a very low degree of influence (or none) on the environmental and human health. Adjusting the properties of epoxy resins with organophosphorus compounds and silver-containing additives is key to the simultaneous improvement of the flame-resistant and antimicrobial properties of advanced epoxy-based materials. These environmentally friendly epoxy resin nanocomposites were manufactured using two additives, a reactive phosphorus-containing bisphenol derived from vanillin, namely, (4-(((4-hidroxyphenyl)amino)(6-oxido-6H-dibenzo[c,e][1,2]oxaphosphinin-6-yl)methyl)-2-methoxyphenyl) phenylphosphonate (BPH), designed as both cross-linking agent and a flame-retardant additive for epoxy resin; and additional silver-loaded zeolite L nanoparticles (Ze-Ag NPs) used as a doping additive to impart antimicrobial activity. The effect of BPH and Ze-Ag NPs content on the structural, morphological, thermal, flame resistance and antimicrobial characteristics of thermosetting epoxy nanocomposites was investigated. The structure and morphology of epoxy nanocomposites were investigated via FTIR spectroscopy and scanning electron microscopy (SEM). In general, the nanocomposites had a glassy and homogeneous morphology. The samples showed a single glass transition temperature in the range of 166-194 °C and an initiation decomposition temperature in the range of 332-399 °C. The introduction of Ze-Ag NPs in a concentration of 7-15 wt% provided antimicrobial activity to epoxy thermosets.
ABSTRACT
Flame-resistant polymer composites were prepared based on polyvinyl alcohol (PVA) as a polymer matrix and a polyphosphonate as flame retardant. Oxalic acid was used as crosslinking agent. LiClO4, BaTiO3, and graphene oxide were also incorporated into PVA matrix to increase the ionic conductivity. The obtained film composites were investigated by infrared spectroscopy, scanning electron microscopy, thermogravimetric analysis, differential scanning calorimetry and microscale combustion tests. Incorporating fire retardant (PFRV), BaTiO3, and graphene oxide (GO) into a material results in increased resistance to fire when compared to the control sample. A thermogravimetric analysis revealed that, as a general trend, the presence of PFRV and BaTiO3 nanoparticles enhances the residue quantity at a temperature of 700 °C from 7.9 wt% to 23.6 wt%. Their dielectric properties were evaluated with Broad Band Dielectric Spectroscopy. The electrical conductivity of the samples was determined and discussed in relation to the LiClO4 content. The electrical properties, including permittivity and conductivity, are being enhanced by the use of LiClO4. Additionally, a relaxation peak has been observed in the dielectric losses at frequencies exceeding 103 Hz. The electrical properties, including permittivity and conductivity, are being enhanced by the use of LiClO4. Additionally, a relaxation peak has been observed in the dielectric losses at frequencies exceeding 103 Hz. Out of the various composites tested, the composite containing 35 wt% of LiClO4 exhibits the highest alternating current (AC) conductivity, with a measured value of 2.46 × 10-3 S/m. Taking into consideration all the aspects discussed, these improved composites are intended for utilization in the manufacturing of Li-Ion batteries.
ABSTRACT
The sustainable development of innovative eco-friendly multifunctional nanocomposites, possessing superior characteristics, is a noteworthy topic. Novel semi-interpenetrated nanocomposite films based on poly(vinyl alcohol) covalently and thermally crosslinked with oxalic acid (OA), reinforced with a novel organophosphorus flame retardant (PFR-4) derived from co-polycondensation in solution reaction of equimolar amounts of co-monomers, namely, bis((6-oxido-6H-dibenz[c,e][1,2]oxaphosphorinyl)-(4-hydroxyaniline)-methylene)-1,4-phenylene, bisphenol S, and phenylphosphonic dichloride, in a molar ratio of 1:1:2, and additionally doped with silver-loaded zeolite L nanoparticles (ze-Ag), have been prepared by casting from solution technique. The morphology of the as prepared PVA-oxalic acid films and their semi-interpenetrated nanocomposites with PFR-4 and ze-Ag was investigated by scanning electron microscopy (SEM), while the homogeneous distribution of the organophosphorus compound and nanoparticles within the nanocomposite films has been introspected by means of energy dispersive X-ray spectroscopy (EDX). It was established that composites with a very low phosphorus content had noticeably improved flame retardancy. The peak of the heat release rate was reduced up to 55%, depending on the content of the flame-retardant additive and the doping ze-Ag nanoparticles introduced into the PVA/OA matrix. The ultimate tensile strength and elastic modulus increased significantly in the reinforced nanocomposites. Considerably increased antimicrobial activity was revealed in the case of the samples containing silver-loaded zeolite L nanoparticles.