Mixed culture sludge has been widely used as a microbial consortium for biohydrogen production. Simple thermal treatment of sludge is usually required in order to eliminate any H2-consuming bacteria that would reduce H2 production. In this study, thermal treatment of sludge was carried out at various temperatures. Electron flow model was then applied in order to assess community structure in the sludge upon thermal treatment for biohydrogen production. Results show that the dominant electron sink was acetate (150-217 e- meq/mol glucose). The electron equivalent (e- eq) balances were within 0.8-18% for all experiments. Treatment at 100 °C attained the highest H2 yield of 3.44 mol H2/mol glucose from the stoichiometric reaction. As the treatment temperature increased from 80 to 100 °C, the computed acetyl-CoA and reduced form of ferredoxin (Fdred) concentrations increased from 13.01 to 17.34 e- eq (1.63-2.17 mol) and 1.34 to 4.18 e- eq (0.67-2.09 mol), respectively. The NADH2 balance error varied from 3 to 10% and the term e-(Fd↔NADH2) (m) in the NADH2 balance was NADH2 consumption (m = -1). The H2 production was mainly via the Fd:hydrogenase system and this is supported with a good NADH2 balance. Using the modified Gompertz model, the highest maximum H2 production potential was 1194 mL whereas the maximum rate of H2 production was 357 mL/h recorded at 100 °C of treatment.

Enhanced Flexibility of Biodegradable Polylactic Acid/Starch Blends Using Epoxidized Palm Oil as Plasticizer.

The brittleness of polylactic acid (PLA) has always limited its usage, although it has good mechanical strength. In this study, flexibility of PLA/starch (PSt) blend was enhanced using epoxidized palm oil (EPO) as the green plasticizer. The PLA/starch/EPO (PSE) blends were prepared while using the solution casting method by fixing the content of starch and varying ratio of EPO. The thermal properties, such as glass transition temperature (Tg), melting temperature (Tm), and crystallization temperature (Tcc) were decreased by increasing the amount of EPO into PSt, indicating that EPO increases the chain mobility. Thermogravimetric analysis (TGA) showed that thermal degradation resistance of PSE was higher when compared to PSt. The mechanical testing revealed that EPO at all contents improved the mechanical properties, such as increment of the elongation-at-break and impact strength. Whereas, dynamic mechanical analysis showed that the addition of filler into PLA decreased the storage modulus of PLA. The carbonyl group of the aliphatic ester remained the same in the PSE blends. The morphological study verified the ductility of PSE blends surface when compared to the brittle surface of PSt. As for the soil burial tests, EPO accelerated the degradation of blends. From these results, it can be concluded that EPO improved the flexibility of PLA blends.