Ag/Ag2O with NIR-Triggered Antibacterial Activities: Photocatalytic Sterilization Enhanced by Low-Temperature Photothermal Effect.

Purpose: A synergistic antibacterial system employing photocatalytic performance and low-temperature photothermal effect (LT-PTT) with the potential for infectious skin wound healing promotion was developed. Methods: Ag/Ag2O was synthesized with a two-step method, and its physicochemical properties were characterized. After its photocatalytic performance and photothermal effect were evaluated under 0.5 W/cm2 808 nm NIR laser irradiation, its antibacterial activities in both planktonic and biofilm forms were then studied in vitro targeting Staphylococcus Aureus (S. aureus), and the biocompatibility was tested with L-929 cell lines afterward. Finally, the animal model of dorsal skin wound infection was established on Sprague-Dawley rats and was used to assess infectious wound healing promotion of Ag/Ag2O in vivo. Results: Ag/Ag2O showed boosted photocatalytic performance and local temperature accumulation compared with Ag2O when exposed to 0.5 W/cm2 808 nm NIR irradiation, which therefore endowed Ag/Ag2O with the ability to kill pathogens rapidly and cleavage bacterial biofilm in vitro. Furthermore, after treatment with Ag/Ag2O and 0.5 W/cm2 808 nm NIR irradiation, infectious wounds of rats realized skin tissue regeneration from a histochemical level. Conclusion: By exhibiting excellent NIR-triggered photocatalytic sterilization ability enhanced by low-temperature photothermal effect, Ag/Ag2O was promising to be a novel, photo-responsive antibacterial agent.

Near-Infrared-Enhanced Dual Enzyme-Mimicking Ag-TiO2-x@Alginate Microspheres with Antibactericidal and Oxygeneration Abilities to Treat Periodontitis.

The effective treatment for periodontitis is to completely and sustainedly eradicate the bacterial pathogens from the complex periodontal pockets. Local sustained-release antibiotics as a complementary treatment after scaling and root planning can sustainedly combat bacterial pathogens in the periodontal pockets to help treat the disease, but the increasing concern of bacterial resistance limits its future use. Here, we reported a local antibacterial system based on microsized multifunctional Ag-TiO2-x encapsulated in alginate (ATA) microspheres. We confirmed that ATA displayed strong photothermally enhanced dual enzyme-mimicking (peroxidase-like and catalase-like) activities and weak photocatalytic activity under 808 nm near-infrared (NIR) irradiation, which could boost the generation of reactive oxygen species (ROS) and O2 in the presence of low-level H2O2. As a result, the ATA/H2O2/NIR system exhibited efficient antibacterial activity against Porphyromonas gingivalis and Streptococcus gordonii in both planktonic and biofilm forms. With the help of ROS, ATA could release Ag+ in concentrations sufficient to inhibit periodontal pathogens as well. Moreover, the in situ-generated oxygen was supposed to alleviate the local hypoxic environment and would help downregulate the lipopolysaccharide-mediated inflammatory response of periodontal stem cells. The in vivo rat periodontitis treatment results demonstrated that the ATA/H2O2/NIR system reduced the bacterial load, relieved inflammation, and improved tissue healing. Our work developed a new local prolonged bactericidal and oxygenation system for enhanced periodontitis. Avoiding the usage of antibiotics and nanomaterials, this strategy showed great promise in adjunctive periodontitis treatment and also in other biomedical applications.

Photothermal-Enhanced Fenton-like Catalytic Activity of Oxygen-Deficient Nanotitania for Efficient and Safe Tooth Whitening.

The growing demand for charming smiles has led to the popularization of tooth bleaching procedures. Current tooth bleaching products with high-concentration hydrogen peroxide (HP, 30-40%) are effective but detrimental due to the increased risk of enamel destruction, tooth sensitivity, and gingival irritation. Herein, we reported a less-destructive and efficient tooth whitening strategy with a low-concentration HP, which was realized by the remarkably enhanced Fenton-like catalytic activity of oxygen-deficient TiO2 (TiO2-x). TiO2-x nanoparticles were synthesized with a modified solid-state chemical reduction approach with NaBH4. The Fenton-like activity of TiO2-x was optimized by manipulating oxygen vacancy (OV) concentration and further promoted by the near-infrared (NIR)-induced photothermal effect of TiO2-x. The TiO2-x sample named BT45 was chosen due to the highest methylene blue (MB) adsorption ability and Fenton-like activity among acquired samples. The photothermal property of BT45 under 808 nm NIR irradiation was verified and its enhancement on Fenton-like activity was also studied. The BT45/HP + NIR group performed significantly better in tooth whitening than the HP + NIR group on various discolored teeth (stained by Orange II, tea, or rhodamine B). Excitingly, the same tooth whitening performance as the Opalescence Boost, a tooth bleaching product containing 40% HP, was obtained by a self-produced bleaching gel based on this novel system containing 12% HP. Besides, negligible enamel destruction, safe temperature range, and good cytocompatibility of TiO2-x nanoparticles also demonstrated the safety of this tooth bleaching strategy. This work indicated that the photothermal-enhanced Fenton-like performance of the TiO2-x-based system is highly promising in tooth bleaching application and can also be extended to other biomedical applications.

hDPSC-laden GelMA microspheres fabricated using electrostatic microdroplet method for endodontic regeneration.

The microsphere system has attracted considerable attention as a stem-cell delivery vehicle in regeneration medicine owing to its injectability, fast substance transfer ability, and mimicry of the three-dimensional native environment. However, suitable biomaterials for preparation of microspheres optimal for endodontic regeneration are still being explored. Owing to its excellent bioactivity and biodegradability, gelatin methacryloyl (GelMA) was used to fabricate hydrogel microspheres by the electrostatic microdroplet method, and the potential of GelMA microspheres applied in endodontic regeneration was studied. The average size of GelMA microspheres encapsulating human dental pulp stem cells (hDPSCs) was ~200 µm, and the Young's modulus was approximately 582.8 ± 66.0 Pa, which was close to that of the natural human dental pulp. The encapsulated hDPSCs could effectively adhere, spread, proliferate, and secrete extracellular matrix proteins in the microspheres, and tended to occupy the outer layer. Moreover, the cell-laden GelMA microsphere system could withstand cryopreservation, and the thawed cells exhibited normal functions. After subcutaneous implantation in a nude mouse model, more vascularized pulp-like tissues were generated in the cell-laden GelMA microsphere group compared with that in the cell-laden bulk GelMA group, and this was accompanied by a suitable degradation rate. The GelMA microspheres showed remarkable performances and great potential as cell delivery vehicles in endodontic regeneration.