Constructing an Anion-Braking Separator to Regulate Local Li+ Solvation Structure for Stabilizing Lithium Metal Batteries.

Lithium metal batteries (LMBs) offer significant advantages in energy density and output voltage, but they are severely limited by uncontrollable Li dendrite formation resulting from uneven Li+ behaviors and high reactivity with potential co-solvent plating. Herein, to uniformly enhance the Li behaviors in desolvation and diffusion, the local Li+ solvation shell structure is optimized by constructing an anion-braking separator, hence dynamically reducing the self-amplifying behavior of dendrites. As a prototypal, two-dimensional lithiated-montmorillonite (LiMMT) is blade-coated on the commercial separator, where abundant -OH groups as Lewis acidic sites and electron acceptors could selectively adsorb corresponding FSI- anions, regulating the solvation shell structure and restricting their migration. Meanwhile, the weakened anion mobility delays the time of breaking electrical neutrality, and the Li nucleation density is quantified through the respective experimental, theoretical and spectroscopical results, providing a comprehensive understanding of modifying anion and cation behaviors on dendritic growth suppression. As anticipated, a long Li plating/stripping lifespan up to 1800 h and a significantly increased average Coulombic efficiency of 98.8% are achieved under 3.0 mAh cm-2. The fabricated high-loading Li-LFP or Li-NCM523 full-cells display the cycle durability with enhanced capacity retention of nearly 100%, providing the instructive guide towards realizing dendrite-free LMBs.

Biomimetic Macrophage Membrane-Camouflaged Nanoparticles Induce Ferroptosis by Promoting Mitochondrial Damage in Glioblastoma.

The increasing understanding of ferroptosis has indicated its role and therapeutic potential in cancer; however, this knowledge has yet to be translated into effective therapies. Glioblastoma (GBM) patients face a bleak prognosis and encounter challenges due to the limited treatment options available. In this study, we conducted a genome-wide CRISPR-Cas9 screening in the presence of a ferroptosis inducer (RSL3) to identify the key driver genes involved in ferroptosis. We identified ALOX15, a key lipoxygenase (LOX), as an essential driver of ferroptosis. Small activating RNA (saRNA) was used to mediate the expression of ALOX15 promoted ferroptosis in GBM cells. We then coated saALOX15-loaded mesoporous polydopamine (MPDA) with Angiopep-2-modified macrophage membranes (MMs) to reduce the clearance by the mononuclear phagocyte system (MPS) and increase the ability of the complex to cross the blood-brain barrier (BBB) during specific targeted therapy of orthotopic GBM. These generated hybrid nanoparticles (NPs) induced ferroptosis by mediating mitochondrial dysfunction and rendering mitochondrial morphology abnormal. In vivo, the modified MM enabled the NPs to target GBM cells, exert a marked inhibitory effect on GBM progression, and promote GBM radiosensitivity. Our results reveal ALOX15 to be a promising therapeutic target in GBM and suggest a biomimetic strategy that depends on the biological properties of MMs to enhance the in vivo performance of NPs for treating GBM.

In-situ catalytic mechanism coupling quantum dot effect for achieving high-performance sulfide anode in potassium-ion batteries.

Though numerous framework structures have been constructed to strengthen the reaction kinetics and durability, the inevitable generation of polysulfide dissolution during conversion-process can cause irreparable destruction to ion-channel and crystal structure integrality, which has become a huge obstacle to the application of metal-sulfide in potassium-ion batteries. Herein, the quantum dot structure with catalytic conversion capability is synchronously introduced into the design of FeS2 anode materials to heighten its K+-storage performance. The constructed quantum dot structure anchored by the graphene with space-confinement effect can shorten the ion diffusion path and enlarge the active area, thus accelerating the K+-ions transmission kinetics and absorption action, respectively. The intermediate phase of formed Fe-nanoclusters possesses high-active catalysis ability, which can effectively suppress the polysulfide shuttle combined with the enhanced absorption effect, fully guaranteeing the structure stability and cycling reversibility. Predictably, the fabricated quantum dot FeS2 can express a prominent advantage in rapid potassiation/depotassiation processes (518.1 mAh g-1, 10 A g-1) and a superior cycling lifespan with gratifying reversible capacity at superhigh rate (177.7 mAh g-1, 9000 cycles, 5 A g-1). Therefore, engineering quantum dot structure with self-induced catalysis action for detrimental polysulfide is an achievable strategy to implement high-performance sulfide anode materials for K-ions accommodation.