Vertical marginal discrepancy of ceramic copings with different ceramic materials, finish lines, and luting agents: an in vitro evaluation.

STATEMENT OF PROBLEM: Prosthetic restorations that fit poorly may affect periodontal health and occlusion. Studies that have evaluated the accuracy of fit of ceramic restorations before and after cementation assessed primarily intracoronal restorations. PURPOSE: This in vitro study evaluated the effect of different finish lines, ceramic manufacturing techniques, and luting agents on the vertical discrepancy of ceramic copings. MATERIAL AND METHODS: Two stainless steel molars were prepared for complete crowns with 2 different finish lines (heavy chamfer and rounded shoulder); each molar was duplicated to fabricate 90 copings. A total of 180 copings generated 18 groups (n=10 for each finish line-coping material-luting agent combination). Luting agents tested included zinc phosphate, resin-modified glass ionomer (Fuji Plus), and resin composite cements (Panavia F). A metal frame was developed on which to screw the stainless steel model and a ceramic coping; the distance (microm) between 2 predetermined points was measured before and after cementation by a profile projector under a torquing force. A 4-way ANOVA with repeated measurements was performed to assess the influence of each factor in the vertical marginal discrepancy: 3 between-coping factors (finish line-coping material-luting agent) and 1 within-coping factor (before and after cementation) (alpha=.05). RESULTS: Procera copings presented the lowest mean values ( P <.05) of vertical marginal discrepancy before and after cementation (25/44 microm) when compared to Empress 2 (68/110 microm) and InCeram Alumina copings (57/117 microm), regardless of any combinations among all finish lines and luting agents tested. CONCLUSION: Considering each factor separately, the ceramic manufacturing technique appeared to be the most important factor tested for the definitive vertical discrepancy of all-ceramic copings, with lower mean values for Procera copings.

Avaliação "in vitro" do desajuste cervical vertical de copings cerâmicos, variando materiais restauradores, términos cervicais e agentes de fixação / Vertical discrepancy of ceramic copings with different ceramic materiais, finish lines and luting agents: an in vitro evaluation

O objetivo desse estudo foi avaliar a discrepância cervical vertical in vitro de copings cerâmicos, variando-se término cervical, o material cerâmico e o agente de fixação. Dois modelos-padrão foram usinados em aço inoxidável nas dimensões de um molar preparado, sendo um com término em chanfro largo e outro em ombro arredondado. Produziram-se cento e vinte e dois troquéis em gesso tipo IV, metade para cada tipo de término. A partir dos mesmos, confeccionaram-se sessenta copings do material Empress 2, sessenta em In Ceram e sessenta em Procera. Resultaram cento e oitenta copings, sendo noventa para cada tipo de término. Os materiais utilizados para a cimentação foram cimento de fosfato de zinco, cimento de ionômero de vidro modificado por resina e cimento resinoso. O conjunto modelo-padrão/coping cerâmico foi parafusado em um dispositivo em forma de morsa, sobre o qual se aplicou torque de 10N antes de cada mensuração. Essa foi feita em um projetor de perfil, registrando-se um valor de ordenada e abscissa em dois pontos pré-determinados, antes (LO) e após (L 1) a cimentação, totalizando trezentas e sessenta leituras. Os resultados foram submetidos à análise de variância para as leituras LO e L 1. Para os resultados antes da cimentação (LO) , houve diferença estatística entre os dois tipos de términos cervicais, os três materiais restauradores, bem como para a interação entre eles. Após a cimentação (L 1), somente a variável material restaurador e sua interação com o tipo de término apresentaram diferenças estatisticamente significantes. Concluiu-se que o término cervical foi significante apenas antes da cimentação, enquanto que o material restaurador foi significante antes e depois da cimentação; também foi significante a interação entre o término cervical e o material restaurador, antes e depois da cimentação.

A comparative study of flexural strength using two composite resins fiber reinforced / Estudo comparativo da resistência à flexão de duas resinas compostas reforçadas por fibra

A finalidade deste estudo foi de avaliar as propriedades mecânicas de duas resinas compostas Charisma (Heraeus Kulzer, Alemanha) e Permalute (Ultradent Products Inc.) e verificar a influência da adição de uma fibra (Ribbond, Ribbond Inc.) na resistência à flexão das duas resinas. Foram preparados 52 corpos-de-prova num dispositivo de aço inoxidável com base retangular, sobre a qual é parafusada uma placa também em aço inoxidável com nove espaços usinados medindo 15mm de comprimento, 2mm de largura e 1mm de espessura, sobre os quais se aplicou as resinas compostas associadas ou não a fibras. Os corpos-de-prova foram divididos em quatro grupos (n=13), sendo o Grupo I somente de resina composta Charisma; Grupo II resina Charisma + Ribbond; Grupo III somente de resina Permalute e Grupo IV de resina Permalute + Ribbond. As amostras foram submetidas ao ensaio de compressão de três pontos para verificar a resisência flexural em um aparelho MTS-810 até à ruptura das mesmas e então avaliadas sob microscopia eletrônica de varredura. Os dados foram submetidos aos testes paramétricos 1-way ANOVA, análise de variância e de Comparação Múltipla de Tukey (5 por cento), após o teste de homogeneidade de variância, teste de Levene, sob nível de significância de 5 por cento. As amostras do Grupo I obtiveram média de 164,71 MPa (d.p. = 21,49 por cento); para o Grupo II, a média de ruptura foi de 292,28 MPa (d.p. = 34,24 por cento); para o Grupo III a média foi de 106,50 MPa (d.p. = 24,02 por cento) e para o Grupo IV os valores médios foram 61,70 MPa (d.p. = 24,92 por cento). Os resultados demonstram que a adição de fibras entrelaçadas aumentou consideravelmente a resistência à flexão, sendo melhor para Charisma + Ribbond do que Permalute + Ribbond. Entretanto, pela análise da região fraturada empregando-se o M.E.V., concluimos que não ocorreu reação química entre as resinas compostas e as fibras, embora não apresente completa separação entre a matriz e as fibras

Aesthetic and adhesive cementation for contemporary porcelain crowns / Cimentação adesiva e estética para coroas de porcelana contemporâneas

The evolution of aesthetic restorative materials has led to the development of new preparation designs and cementation protocols. While conventional cements were able to provide mechanical and macromechanical retention for restorations with limited aesthetic expectations, resin cements with micromechanical retention have been formulated as aesthetic alternatives. The objective of the present article is to establish the differences between conventional and adhesive crown cementation techniques, as well as to provide guidelines for reducing postoperative sensitivity and improving aesthetic and functional results

Effect of the surface treatment of plain carbon fiber posts on the retention of the composite core: an in vitro evaluation / Efeito do tratamento superficial de pinos de fibra de carbono lisos na retençäo da resina de preenchimento: uma avaliaçäo in vitro

Foi avaliado o possível efeito de tratamentos superficiais em pinos de fibra de carbono lisos, quando comparados aos pinos serrilhados, na retençäo à resina composta empregada na confecçäo de núcleos de preenchimento. Foram utilizados cinqüenta pinos de fibra de carbono, divididos em cinco grupos: os quatro primeiros grupos eram constituídos por pinos do tipo liso, cujas superfícies foram tratadas, e o último grupo por dez pinos do tipo serrilhado. Foram desenvolvidas matrizes de resina acrílica com um leito ajustado para conter o pino, com um alargamento na porçäo coronária para posterior preenchimento com resina composta. Após o tratamento superficial, todos os pinos receberam camadas de "primer", foram secos e entäo ajustados à matriz de resina, colocando-se a resina composta autopolimerizável na porçäo coronária para um núcleo de preenchimento de 3 mm. As amostras foram submetidas a termociclagem e armazenadas em água destilada por uma semana. Os espécimes foram testados por meio de ensaios mecânicos de traçäo, à velocidade de 0,5 mm/min, até o deslocamento do conjunto ou a fratura da resina do núcleo...

An S.E.M. evaluation of carbon-fiber post and core resin interface, before and after an in vitro test / Avaliação por microscopia eletrônica de varredura da interface entre resina e pino de fibra de carbono, antes e depois de um teste in vitro

Este estudo tem o propósito de avaliar o efeito de tratamentos superficiais à superfície de pinos de fibra de carbono lisos na retenção da resina de preenchimento, comparando com a retenção aos pinos de carbono de superfície serrilhada. Cinquenta pinos de fibra de carbono foram divididos em cinco grupos: os primeiros quatro grupos continham pinos de fibra de carbono lisos e o último grupo, dez pinos de fibra de carbono de superfície serrilhada. Os pinos de fibra de carbono lisos receberam os seguintes tratamentos superficiais: jateamento com óxico de alumínio (Grupo A); tratamento com pontas diamantadas de granulação média (Grupo B); tratamento com pontas diamantadas para facetas laminadas (Grupo C); usinagem da extremidade coronária (Grupo D); o Grupo E consistia de pinos de fibra de carbono serrilhados pelo fabricante. Uma matriz de resina acrílica foi desenvolvida para que os pinos ficassem bem ajustados, deixando um espaço na extremidade coronária para acomodar uma resina autopolimerizável para núcleos de preenchimento. Após o tratamento superficial foi aplicado um primer, os pinos foram secos e adaptados à matriz para receber um núcleo de resina composta com 3 mm de altura. Os espécimes receberam ciclagem térmica e foram armazenados em água destilada durante uma semana. O teste de tração foi executado em uma máquina Instron até o deslocamento ou a fratura do mesmo. Foi feita uma análise da superfície dos pinos sob microscopia eletrônica de varredura (M.E.V.) sob aumento de 500X, antes e após o teste de tração. Após o teste de tração, os valores médios de retenção foram menores para o Grupo B quando comparados aos demais grupos. A adesão foi maior para os Grupos A e B que para os Grupos com retenção macroscópica (C, D and E). A avaliação em M.E.V. revelou que os grupos sem retenção macroscópica (A and B) apresentaram maior superfície de adesão da resina composta de preenchimento quando comparada à retenção dos grupos com retenção macroscópica (C, D and E)

A prótese adesiva como soluçäo clínica em desdentados parciais Parte I. Anterior / Adhesive prosthesis as a clinical solution in partial dentures. Part I. Anterior

Os autores, após fazerem uma revisäo da literatura sobre próteses adesivas, mostram sua técnica de utilizaçäo, indicaçäo e contra-indicaçäo. Para ilustrar mostram um caso clínico anterior. Concluem que esta técnica representa uma alternativa na clínica odontológica, devido à conservaçäo da estrutura dental, uma melhor estética e um baixo custo. Um dos fatores limitantes de sua utilizaçäo é a oclusäo, tornando necessário um cuidadoso planejamento. Finalmente, afirmam que o pequeno tempo de utilizaçäo na clínica restringe seu emprego como manobra de rotina

A prótese adesiva em desdentados parciais. Parte II. Posterior, soluçäo clínica / Adhesive prosthesis in partial edentulous patients. Part II. Posterior (clinical solution)

Os autores, após fazerem uma revisäo da literatura sobre as próteses adesivas, mostram a sua técnica de utilizaçäo indicaçöes e contra-indicaçöes. Para ilustrar mostram um caso clínico posterior. Concluem que esta técnica representa uma alternativa na clínica odontológica, devido à conservaçäo da estrutura dental, uma melhor estética e um baixo custo. Como uma das limitaçöes da prótese adesiva, temos o fator oclusäo, tornando necessário um cuidadoso planejamento. Finalmente, afirmam que o pequeno tempo de utilizaçäo na clínica restringe seu emprego como manobra de rotina