Influence of Flexible and Textile Substrates on Frequency-Selective Surfaces (FSS).

Frequency-selective surfaces (FSS) are two-dimensional geometric structures made of conductive materials that selectively transmit or reflect electromagnetic waves. In this paper, flexible FSS made on textile and film substrates is presented and compared to show the effect of the texture associated with the type of substrate on the shielding properties. Three geometries of patterns of squares in the border, inversion of squares in the border, and circles with a border were used, and the patterns were made by the silver paste screen printing technique. Microscopic analysis (SEM and optical) was performed to determine the degree of substrate coverage and the actual geometry of the pattern. The resistance per square of the obtained patterns was about 50 mΩ/□. The shielding properties of FSS were simulated in Comsol Multiphysics 6.2 software and then measured by the antenna method. Selective textile filters were obtained, depending on the pattern used, with one or two modals with a transmission attenuation of about 15 dB. The paper analyzes the effect of the substrate and the screen printing technique used on the shielding properties of the flexible FSS.

Electrical Conductance Mechanism of Silver-Polyacrylonitrile Nanocomposite Fibers.

This paper presents the mechanism of electrical conductivity in nanocomposite polyacrylonitrile (PAN) fibers modified with silver nanoparticles (AgNPs). Fibers were formed by the wet-spinning method. The nanoparticles were introduced into the polymer matrix as a result of direct synthesis in the spinning solution from which the fibers were obtained, thereby influencing the chemical and physical properties of the polymer matrix. The structure of the nanocomposite fibers was determined using SEM, TEM, and XRD, and the electrical properties were determined using the DC and AC methods. The conductivity of the fibers was electronic and based on the percolation theory with tunneling through the polymer phase. This article describes in detail the influence of individual fiber parameters on the final electrical conductivity of the PAN/AgNPs composite and presents the mechanism of conductivity.

Correlation between Microstructure and Chemical Composition of Zinc Oxide Gas Sensor Layers and Their Gas-Sensitive Properties in Chlorine Atmosphere.

In this article, we present results concerning the impact of structural and chemical properties of zinc oxide in various morphological forms and its gas-sensitive properties, tested in an atmosphere containing a very aggressive gas such as chlorine. The aim of this research was to understand the mechanism of chlorine detection using a resistive gas sensor with an active layer made of zinc oxide with a different structure and morphology. Two types of ZnO sensor layers obtained by two different technological methods were used in sensor construction. Their morphology, crystal structure, specific surface area, porosity, surface chemistry and structural defects were characterized, and then compared with gas-sensitive properties in a chlorine-containing atmosphere. To achieve this goal, scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and photoluminescence spectroscopy (PL) methods were used. The sensing properties of obtained active layers were tested by the temperature stimulated conductance method (TSC). We have noticed that their response in a chlorine atmosphere is not determined by the size of the specific surface or porosity. The obtained results showed that the structural defects of ZnO crystals play the most important role in chlorine detection. We demonstrated that Cl2 adsorption is a concurrent process to oxygen adsorption. Both of them occur on the same active species (oxygen vacancies). Their concentration is higher on the side planes of the zinc oxide crystal than the others. Additionally, ZnO sublimation process plays an important role in the chlorine detection mechanism.

Plasma Jets Fabricated in Low-Temperature Cofired Ceramics for Gold Nanoparticles Synthesis.

In this article, we present a development of atmospheric pressure plasma jets (APPJs) for modification of liquid solutions. APPJs were fabricated in low temperature cofired ceramics (LTCC) technology. During the measurements, plasma jets worked under various flowing gases, which can be used to produce plasma activated water. In addition, owing to the plasma treatment, it was possible to decrease the time of a synthesis of gold nanoparticles (AuNPs) without the use of additional hazardous reagents. The mechanism of gold nanoparticles formation in cold nitrogen plasma is also presented.

Multifunctional Nanocomposite Cellulose Fibers Doped in Situ with Silver Nanoparticles.

This paper presents a method for the preparation of nanocomposite cellulose fibers doped with silver nanoparticles (AgNPs), as well as the effect of silver nanoparticles on the structure and properties of fibers. The fibers were obtained by an environmentally friendly method using N-Methylmorpholine N-oxide (NMMO) as a solvent, in a non-polluting closed system. Doping with silver nanoparticles was carried out as a direct (in situ) reduction of Ag⁺ ions in the presence of a stabilizing agent during the preparation of the spinning solution. SEM images of the surface and cross section of the fibers showed that the distribution of nanoparticles in the fibers' volume was uniform. The fibers exhibited very good antibacterial properties in relation to Staphylococcus aureus, Escherichia coli, Acinetobacter baumannii, and Candida albicans. Flammability analysis showed that the fibers were subjected to a one-stage combustion process and that the silver nanoparticles reduced the heat release rate (HRR) of the fibers by 36%. TG studies showed that the modification of cellulose fibers with silver nanoparticles promoted the formation of mill scale in the combustion of fibers, which was directly related to the reduction of flammability. Tests of the electrical properties showed that the linear resistance of cellulose fibers containing 3 wt % silver was 108 Ω/cm.

The Preparation and Characterization of Polyacrylonitrile-Polyaniline (PAN/PANI) Fibers.

The paper presents a method of modifying polyacrylonitrile (PAN) fibers using polyaniline (PANI). The PAN fibers were doped with polyaniline that was obtained in two different ways. The first consisted of doping a spinning solution with polyaniline that was synthesized in an aqueous solution (PAN/PANI blended), and the second involved the synthesis of polyaniline directly in the spinning solution (PAN/PANI in situ). The obtained fibers were characterized by the methods: X-ray powder diffraction (XRD), scanning electron microscope (SEM), fourier-transform infrared spectroscopy (FTIR), thermogravimetry (TG) and differential scanning calorimetry (DSC). Analysis of the results showed strong interactions between the nitrile groups of polyacrylonitrile and polyaniline in the PAN/PANI in situ fibers. The results of mechanical strength tests indicated that the performance of the PAN/PANI mixture significantly improved the mechanical parameters of polyaniline, although these fibers had a weaker strength than the unmodified PAN fibers. The fibers obtained as a result of the addition of PANI to PAN were dielectric, whereas the PANI-synthesized in situ were characterized by a mass-specific resistance of 5.47 kΩg/cm².

Deposition of Zinc Oxide on Different Polymer Textiles and Their Antibacterial Properties.

A surface modification of polyamide 6 (PA), polyethylene terephthalate (PET) and polypropylene (PP) textiles was performed using zinc oxide to obtain antibacterial layer. ZnO microrods were synthesized on ZnO nanoparticles (NPs) as a nucleus centers by chemical bath deposition (CBD) process. Scanning Electron Microscopy (SEM) and X-ray diffraction (XRD) indicated that wurzite ZnO microrods were obtained on every sample. Differential Scanning Calorimetry (DSC), Fourier Transform Infrared Spectroscopy (FTIR), Atomic Force Microscopy (AFM) and Liquid Absorption Capacity (LAC) analysis indicate that the amount and structure of antibacterial layer is dependent on roughness and wettability of textile surface. The rougher and more hydrophilic is the material, the more ZnO were deposited. All studied textiles show significant bactericidal activity against Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus). A possible mechanism and difference in sensitivity between Gram-negative and Gram-positive bacteria to ZnO is discussed. Considering that antibacterial activity of ZnO is caused by Reactive Oxygen Species (ROS) generation, an influence of surface to volume ratio and crystalline parameters is also discussed.

The Relationship between the Mechanism of Zinc Oxide Crystallization and Its Antimicrobial Properties for the Surface Modification of Surgical Meshes.

Surgical meshes were modified with zinc oxide (ZnO) using a chemical bath deposition method (CBD) at 50 °C, 70 °C, or 90 °C, in order to biologically activate them. Scanning electron microscopy (SEM), mass changes, and X-ray diffraction measurements revealed that at low temperatures Zn(OH)2 was formed, and that this was converted into ZnO with a temperature increase. The antimicrobial activity without light stimulation of the ZnO modified Mersilene™ meshes was related to the species of microorganism, the incubation time, and the conditions of the experiment. Generally, cocci (S. aureus, S. epidermidis) and yeast (C. albicans) were more sensitive than Gram-negative rods (E. coli). The differences in sensitivity of the studied microorganisms to ZnO were discussed. The most active sample was that obtained at 90 °C. The mechanism of antimicrobial action of ZnO was determined by various techniques, such as zeta potential analysis, electron paramagnetic resonance (EPR) spectroscopy, SEM studies, and measurements of Zn(II) and reactive oxygen species (ROS) concentration. Our results confirmed that the generation of free radicals was crucial, which occurs on the surface of crystalline ZnO.

Microfluidical Microwave Reactor for Synthesis of Gold Nanoparticles.

Microwave treatment can reduce the time of selected syntheses, for instance of gold nanoparticles (AuNPs), from several hours to a few minutes. We propose a microfluidic structure for enhancing the rate of chemical reactions using microwave energy. This reactor is designed to control microwave energy with much higher accuracy than in standard devices. Thanks to this, the influence of microwave irradiation on the rate of chemical reactions can be investigated. The reactor consists of a transmission line surrounded by ground metallization. In order to deliver microwave energy to the fluid under test efficiently, matching networks are used and optimized by means of numerical methods. The monolithic device is fabricated in the low temperature co-fired ceramics (LTCC) technology. This material exhibits excellent microwave performance and is resistant to many chemical substances as well as high temperatures. Fabrication of the devices is described in detail. Measurements of microwave parameters are performed and differences between simulation and experiment results are discussed. Finally, the usefulness of the proposed device is proved in exemplary synthesis.