1.
Braz Oral Res ; 31: e29, 2017 04 10.
Article in English | MEDLINE | ID: mdl-28403332

ABSTRACT

This study evaluates the influence of root dentin treatment with NaOCl alone and combined with EDTA, with and without ultrasound activation, on the push-out bond strength (BS) of fiber-reinforced posts in weakened roots, cemented with RelyX or Panavia. The root canals of 42 maxillary canines were instrumented with Reciproc and 2.5% NaOCl. In the coronal 12mm of all canals, experimental weakening of the roots was produced by reducing dentin thickness with 2.44mm diameter diamond burs. The roots were assigned to 3 groups (n = 14) according to root dentin treatment: 2.5% NaOCl; 2.5% NaOCl + 17% EDTA; and 2.5% NaOCl + 17% EDTA, with solutions agitated using passive ultrasonic irrigation. After cementation of the fiber-reinforced posts the roots were divided in thirds. The first slice of each third was used for the push-out BS test, the second slice for confocal laser scanning microscopy and dentin microhardness (Knoop) analysis. Data were analysed by a two-way ANOVA and Tukey test (a = 0.05). NaOCl + EDTA provided highest BS values than NaOCl (p < 0.0001). Specimens cemented with Panavia presented significantly higher BS than those with RelyX in the three root thirds (p < 0.0001). The highest BS values occurred in the cervical third (p < 0.001). Ultrasound-activated NaOCl + EDTA promoted the greatest reduction in dentin microhardness, followed by NaOCl/EDTA and NaOCl. Ultrasonic activation of NaOCl and EDTA reduced root dentin microhardness, but did not improve the push-out BS of resin-based cements. Panavia presented higher BS than RelyX. RelyX was not influenced by the root dentin treatment protocols.


Subject(s)
Dental Bonding/methods , Dentin/drug effects , Edetic Acid/chemistry , Resin Cements/chemistry , Sodium Hypochlorite/chemistry , Tooth Root/drug effects , Acid Etching, Dental/methods , Analysis of Variance , Dental Restoration Failure , Dentin/radiation effects , Hardness Tests , Humans , Materials Testing , Microscopy, Confocal , Post and Core Technique , Random Allocation , Reference Values , Reproducibility of Results , Root Canal Irrigants/chemistry , Root Canal Preparation/methods , Statistics, Nonparametric , Surface Properties/drug effects , Tooth Root/radiation effects , Ultrasonic Therapy
2.
Braz Dent J ; 22(4): 299-305, 2011.
Article in English | MEDLINE | ID: mdl-21861029

ABSTRACT

The aim of this study was to evaluate the biocompatibility of sealers used in apical surgery in rat subcutaneous tissue. Sterile polyethylene tubes were filled with the following sealers: Sealapex, Sealapex with addition of zinc oxide, Sealer 26, Sealer 26 with thicker consistency (greater powder-to-resin ratio) and White MTA. The tubes were implanted in the dorsum of male rats and after 7, 21 and 42 days, the animals were killed, obtaining 5 specimens for each sealer in each evaluation period. The lateral surface of the tube was used as negative control. The inflammatory reaction to contact with the sealers was classified as absent, mild, moderate and severe. At 7 days, all sealers caused similar inflammatory reactions in the connective tissue of the animals, with most specimens presenting a moderate to intense chronic inflammatory reaction, with presence of multinucleated giant cells. At 21 days, Sealer 26 and Sealer 26 with thicker consistency presented more intense inflammatory reaction (p=0.004), whereas after 42 days, the inflammatory reaction ranged from absent to mild with statistically similar results for both materials (p=0.08). Except for MTA, all sealers presented foreign-body granulomatous reaction at 42 days. All sealers but Sealapex presented a statistically significant decrease of the inflammatory reaction over time. In conclusion, all sealers caused moderate to severe inflammation in the earlier evaluation period. However, Sealer 26 and Sealer 26 with thicker consistency caused more intense inflammatory reactions after 21 days of contact with the tissues and no granulomatous reaction was observed for MTA at the final period of analysis.


Subject(s)
Biocompatible Materials/pharmacology , Root Canal Filling Materials/pharmacology , Subcutaneous Tissue/drug effects , Aluminum Compounds/pharmacology , Animals , Bismuth/pharmacology , Calcium Compounds/pharmacology , Calcium Hydroxide/pharmacology , Cellulitis/chemically induced , Drug Combinations , Giant Cells/pathology , Granuloma, Foreign-Body/chemically induced , Lymphocytes/pathology , Macrophages/pathology , Male , Materials Testing , Necrosis , Oxides/pharmacology , Rats , Rats, Wistar , Salicylates/pharmacology , Silicates/pharmacology , Subcutaneous Tissue/pathology , Time Factors , Viscosity , Zinc Oxide/pharmacology