ABSTRACT
The development of new mesoporous frits for reference electrodes to overcome the limitations of cross-contamination and screening effect is essential for many electrochemical measurements. Available frit-based reference electrodes (e.g., mesoporous, microporous) still suffer from cross-contamination and/or errors in electrochemical measurements. In this work, a mesoporous glass-ceramic composite is prepared to mitigate such limitations. Mesoporous glass-ceramic frits were prepared from low-cost materials (i.e., borosilicate and kaolin) at relatively low temperatures (750-850 °C). The prepared glass-ceramic frits were characterized using scanning electron microscopy (SEM), impedance measurements, and nitrogen sorption isotherms. The developed mesoporous glass-ceramic composites are characterized by a high chemical resistance against corrosive materials and a low thermal expansion. Reference electrodes constructed with the developed mesoporous glass-ceramic frits exhibited a low flow rate of 0.002 ± 0.001 to 0.41 ± 0.06 µL h-1 and high potential stability as well as very small potential drift of -2.4 ± 0.2 to -4.9 ± 0.2 µV h-1. Mesoporous glass-ceramic based reference electrodes exhibited average potential variations of 13 ± 3 mV over the concentration range of 1 mM to 0.1 M KCl. This indicates that mesoporous glass-ceramic frit-based reference electrodes exhibited a much lower flow rate compared to available microporous frit-based reference electrodes. Moreover, the developed mesoporous ceramic-based reference electrodes exhibited a 4-15-fold improvement in potential variations and a large improvement in potential stability in comparison with the reported mesoporous-frit-based reference electrodes.