ABSTRACT
A theoretical study of the mechanisms of electroluminescence (EL) generation in photoactive molecules with donor and acceptor centers linked by saturated σ-bonds (molecules of the Aviram-Ratner-type) is presented. The approach is based on the kinetics of single-electron transitions between many-body molecular states. This study shows that the EL polarity arises due to asymmetric coupling of molecular orbitals of the photochromic part of the molecule to the electrodes. The gate voltage controls the power of the EL through the occupancy of the excited singlet state. The shifting of the orbital energies forms a resonant or a non-resonant path for the transmission of electrons through the molecule. The action of the gate voltage is reflected in specific critical voltages. An analytical dependence of the critical voltages on the energies of molecular states involved in the formation of EL, as well as on the gate voltage, was derived for both positive and negative polarities. Conditions under which the gate voltage lowers the absolute value of the bias voltage that is responsible for the activation of the resonance mechanism of EL formation were also established. This is an important factor in control of EL in molecular junctions.
ABSTRACT
Ba0.85Ca0.15Zr0.10Ti0.90O3 (BCZT) relaxor ferroelectric ceramics exhibit enhanced energy storage and electrocaloric performances due to their excellent dielectric and ferroelectric properties. In this study, the temperature-dependence of the structural and dielectric properties, as well as the field and temperature-dependence of the energy storage and the electrocaloric properties in BCZT ceramics elaborated at low-temperature hydrothermal processing are investigated. X-ray diffraction and Raman spectroscopy results confirmed the ferroelectric-paraelectric phase transition in the BCZT ceramic. At room temperature and 1 kHz, the dielectric constant and dielectric loss reached 5000 and 0.029, respectively. The BCZT ceramic showed a large recovered energy density (W rec) of 414.1 mJ cm-3 at 380 K, with an energy efficiency of 78.6%, and high thermal-stability of W rec of 3.9% in the temperature range of 340-400 K. The electrocaloric effect in BCZT was explored via an indirect approach following the Maxwell relation at 60 kV cm-1. The significant electrocaloric temperature change of 1.479 K at 367 K, a broad temperature span of 87 K, an enhanced refrigerant capacity of 140.33 J kg-1, and a high coefficient of performance of 6.12 obtained at 60 kV cm-1 make BCZT ceramics potentially useful coolant materials in the development of future eco-friendly solid-state refrigeration technology.