ABSTRACT
Sheets of high-density polyethylene (HDPE) loaded with magnesium oxide in micro and nano were synthesized with different weight percentages of micro-MgO (0,5,10,20 and 30% by weight) and nano-MgO (5 and 30%) and shaped in form of disc and dog bone shape. The morphological, mechanical, and attenuation characteristics of each concentration were determined. The linear attenuation coefficients (LAC) of the prepared discs were calculated using a well-calibrated scintillation detector and five standard gamma-ray point sources (241Am, 133Ba, 137Cs, 60Co and 152Eu). The LAC was theoretically calculated for HDPE/micro-MgO composites using XCOM software. A good agreement between the theoretical and experimental results was observed. The comparison between micro and nano-MgO as a filler in HDPE was evaluated. The results proved that the loaded nano-MgO in different proportions of HDPE produced greater attenuation coefficients than its micro counterpart. The addition of nano MgO with different weight percentage led to a significant improvement in the mechanical properties of HDPE, the ultimate force and ultimate stress increased as the concentration of nano MgO increased, and the young modulus of HDPE also increased with increasing concentration of micro and nano MgO.
ABSTRACT
We report photocatalytic degradation studies on Navy Blue HE2R (NB) dye on significant details as a representative from the class of azo dyes using functional nanosystems specifically designed to allow a strong photocatalytic activity. A modified sol-gel route was employed to synthesize Au and gamma-Fe2O3 modified TiO2 nanoparticles (NPs) at low temperature. The attachment strategy is better because it allows clear surface of TiO2 to remain open for photo-catalysis. X-ray diffraction, Raman and UV-VIS spectroscopy studies showed the presence of gold and iron oxide phases along-with the anatase TiO2 phase. TEM studies showed TiO2 nanocomposite particles of size approximately 10-12 nm. A detailed investigation on heterogeneous photocatalytic performance for Navy Blue HE2R dye was done using the as-synthesized catalysts Au:TiO2 and gamma-Fe2O3:TiO2 in aqueous suspension under 8 W low-pressure mercury vapour lamp irradiation. Also, the photocatalytic degradation of Amranth and Orange G azo dyes were studied. The surface modified TiO2 NPs showed significantly improved photocatalytic activity as compared to pure TiO2. Exposure of the dye to the UV light in the presence of pure and gold NPs attached TiO2 catalysts caused dye degradation of about approximately 20% and approximately 80%, respectively, in the first couple of hours. In the presence of gamma-Fe2O3 NPs attached TiO2, a remarkable approximately 95% degradation of the azo dye was observed only in the first 15 min of UV exposure. The process parameters for the optimum catalytic activity are established which lead to a complete decoloration and substantial dye degradation, supported by the values of the Chemical Oxygen Demand (COD) approximately 93% and Total Organic Carbon (TOC) approximately 65% of the treated dye solution after 5 hours on the employment of the UV/Au:TiO2/H2O2 photocatalytic process.