Valorizing the Unexplored Filtration Waste of Brewing Industry for Green Silver Nanocomposite Synthesis.

The brewing industry generates a substantial amount of by-products rich in polyphenols, carbohydrates, sugars, sulfates, nitrogen compounds, organic carbon, and several elements, including chlorine, magnesium, and phosphorus. Although limited quantities of these by-products are used in fertilizers and composts, a large amount is discarded as waste. Therefore, it is crucial to identify different ways of valorizing the by-products. Research regarding the valorization of the brewery by-products is still in its nascent stage; therefore, it still has high potential. Herein, we report the valorization of the brewery by-product from the filtration stage of the brewing process (BW9) to synthesize silver nanocomposites as this waste has remained largely unexplored. The BW9 nanocomposites have been compared to those obtained from the brewery product B. The chemical composition analysis of BW9 and B revealed several organic moieties capable of reducing metal salts and capping the formed nanoparticles. Therefore, the brewery waste from stage 9 was valorized as a precursor and added to silver-based precursor at various temperatures (25, 50, and 80 °C) and for various time periods (10, 30, and 120 min) to synthesize silver nanocomposites. The nanocomposites obtained using BW9 were compared to those obtained using the main product of the brewing industry, beer (B). Synthesized nanocomposites composed of AgCl as a major phase and silver metal (Agmet) was incorporated in minor quantities. In addition, Ag3PO4 was also found in B nanocomposites in minor quantities (up to 34 wt.%). The surface morphology depicted globular nanoparticles with layered structures. Small ball-like aggregates on the layer representative of Ag3PO4 were observed in B nanocomposites. The surface of nanocomposites was capped with organic content and functional groups present in the brewery products. The nanocomposites demonstrated high antibacterial activity against Escherichia coli (E. coli), with BW9 nanocomposites exhibiting a higher activity than B nanocomposites.

Effect of Microwave Treatment in a High Pressure Microwave Reactor on Graphene Oxide Reduction Process-TEM, XRD, Raman, IR and Surface Electron Spectroscopic Studies.

Reduced graphene oxide (rGO) was prepared by chemical reduction of graphene oxide (GO) (with a modified Hummers method) in aqueous solutions of hydrazine (N2H4), formaldehyde (CH2O), formic acid (HCO2H) accompanied by a microwave treatment at 250 °C (MWT) by a high pressure microwave reactor (HPMWR) at 55 bar. The substrates and received products were investigated by TEM, XRD, Raman and IR spectroscopies, XPS, XAES and REELS. MWT assisted reduction using different agents resulted in rGOs of a large number of vacancy defects, smaller than at GO surface C sp3 defects, oxygen groups and interstitial water, interlayer distance and diameter of stacking nanostructures (flakes). The average number of flake layers obtained from XRD and REELS was consistent, being the smallest for CH2O and then increasing for HCO2H and N2H4. The number of layers in rGOs increases with decreasing content of vacancy, C sp3 defects, oxygen groups, water and flake diameter. MWT conditions facilitate formation of vacancies and additional hydroxyl, carbonyl and carboxyl groups at these vacancies, provide no remarkable modification of flake diameter, what results in more competitive penetration of reducing agent between the interstitial sites than via vacancies. MWT reduction of GO using a weak reducing agent (CH2O) provided rGO of 8 layers thickness.

Valorization of Brewery Wastes for the Synthesis of Silver Nanocomposites Containing Orthophosphate.

Brewery wastes from stage 5 (Wort precipitate: BW5) and stage 7 (Brewer's spent yeast: BW7) were valorized for the synthesis of silver phosphate nanocomposites. Nanoparticles were synthesized by converting silver salt in the presence of brewery wastes at different temperatures (25, 50, and 80 °C) and times (10, 30, and 120 min). Unexpectedly, BW7 yielded Ag3PO4 nanoparticles with minor contents of AgCl and Ag metal (Agmet). Contrastingly, BW5 produced AgCl nanoparticles with minor amounts of Ag3PO4 and Agmet. Nanocomposites with different component ratios were obtained by simply varying the synthesis temperature and time. The morphology of the nanocomposites contained ball-like structures representative of Ag3PO4 and stacked layers and fused particles representing AgCl and Agmet. The capping on the nanoparticles contained organic groups from the brewery by-products, and the surface overlayer had a rich chemical composition. The organic overlayers on BW7 nanocomposites were thinner than those on BW5 nanocomposites. Notably, the nanocomposites exhibited high antibacterial activity against Escherichia coli ATCC 25922. The antibacterial activity was higher for BW7 nanocomposites due to a larger silver phosphate content in the composition and a thin organic overlayer. The growth of Agmet in the structure adversely affected the antimicrobial property of the nanocomposites.