High-Performance Organic Solar Modules via Bilayer-Merged-Annealing Assisted Blade Coating.

Although encouraging progress is being made on spin-coated prototype cells, organic solar cells (OSCs) still face significant challenges, yet to be explored, for upscaling the multi-stacked photoactive layers in the construction of large-area modules. Herein, high-performance opaque and semitransparent organic solar modules are developed via a bilayer-merged-annealing (BMA)-assisted blade-coating strategy, achieving impressive efficiencies of 14.79% and 12.01% with respect to active area of 18.73 cm2 , which represent the best organic solar minimodules so far. It is revealed that the BMA strategy effectively resolves the de-wetting issues between polar charge transport layer solution and non-polar bulk heterojunction blends, hence improving the film coverage, along with electronic and electric contacts of multi-stacked photoactive layers. As result, organic solar modules coated under ambient conditions successfully retain the high-efficiency of small-area cells upon 312 times area scaling-up. Overall, this work provides a facile and effective method to fabricate high-performance organic solar modules under ambient conditions.

Self-Assembled Donor-Acceptor Dyad Molecules Stabilize the Heterojunction of Inverted Perovskite Solar Cells and Modules.

The heterointerface between a semiconducting metal oxide and a perovskite critically impacts on the overall performance of perovskite solar cells (PVSCs). Herein, we report a feasible yet effective strategy to suppress the interfacial reaction between nickel oxide and the perovskite via chemical passivation with self-assembled dyad molecules, which leads to the simultaneous improvement of the power conversion efficiencies (PCEs) and operational lifetimes of inverted PVSCs. As a result, inverted PVSCs consisting of simple methylammonium iodide perovskites have achieved an excellent PCE of 20.94% and decent photostability with 93% of the initial value after 600 h of 1 sun equivalent illumination. Moreover, this strategy can be readily translated into slot-die fabrication of perovskite modules, achieving a high PCE of 14.90% with an area of 19.16 cm2 (no shade in the interconnecting area) and a geometrical fill factor of 93%. Overall, this work provides an effective strategy to stabilize the vulnerable heterointerface in PVSCs.