ABSTRACT
Methyl orange (MO) is a common anionic azo dye that is harmful to the environment and biology, so it must be treated innocuously before it can be discharged. Adsorption is an effective method to remove anionic dyes. Nanotube mineral is a natural one-dimensional adsorption material, and its unique morphology and structure endow it with good adsorption capacity. Although there are many related studies, there is a lack of in-depth discussions on the influence of nanotube's composition and structure on the adsorption of dyes and other pollutants. In this paper, two kinds of natural one-dimensional silicate minerals [halloysite nanotubes (HNTs) and chrysotile nanotubes (ChNTs)] with similar morphology but slightly different compositions and crystal structures were used as adsorbents, and MO solution was used as simulate pollutants. It is the first time to discuss in depth the influence of the composition and structure of nanotube minerals on their charge properties and the adsorption performance of methyl orange dyes. It is found that HNTs and ChNTs have different adsorption capacity due to the difference of electronegativity between Al3+ and Mg2+ in the crystal, so they possess negative and positive charges respectively in near-neutral solution, which leads to the adsorption capacity of MO by ChNTs with positive charges which is greater than that of HNTs.
ABSTRACT
Nano zero-valent iron has drawn great attention for the degradation of organic dyes due to its high reactivity, large specific surface area, lightweight, and magnetism. However, the aggregation and passivation of iron nanoparticles may prohibit the wide use of it. A new composite material was prepared by loading nano zero-valent iron (nZVI) on montmorillonite (MMT) to overcome the above shortcomings and it was further used for the removal of Rhodamine 6G (Rh 6G) under microwave treatment in the present work. The effects of various parameters, including the initial concentration of Rh 6G, microwave power, and pH value were investigated. The new composite material (nZVI/MMT) showed an excellent degradation ability for removing Rh 6G, and the removal amount reached 500 mg/g within 15 min. The degradation rate reached 0.4365 min-1, significantly higher than most previous reports using other removal methods for Rh 6G.
ABSTRACT
Nanoscale zero valent iron has been a widespread concern in various fields due to its large specific surface area and high reactivity. However, nanoscale zero valent iron (nZVI) is very likely to aggregate and be oxidized, which limit its wide application in industry. Most clay minerals have a large adsorption capacity of cations due to their negative charges and high specific surface areas. In the present work, nZVI was loaded onto two typical clay minerals: kaolinite and sepiolite, to inhibit its oxidation and aggregation. The composites were applied to degrade Rhodamine 6G (Rh 6G) under microwave irradiation. The effects of pH value and microwave power on degradation were studied. The results showed that the removal amount of Rh 6G by nZVI/kaolinite was 110 mg/g in 15 min, while it reached 300 mg/g by nZVI/sepiolite. The difference between these two composites was mostly determined by the structures of these two clay minerals.