ABSTRACT
Glove tear or perforation is a common occurrence during various activities that require gloves to be worn, posing a significant risk to the wearer and possibly others. This is vitally important in a clinical environment and particularly during surgical procedures. When a glove perforation occurs (and is noticed), the glove must be replaced as soon as possible; however, it is not always noticeable. The present article is focused on the design and development of a novel fluorescence-based sensing mechanism, which is integrated within the glove topology, to help alert the wearer of a perforation in situ. We hypothesized that natural rubber gloves with curcumin infused would yield fluorescence when the glove is damaged, particularly when torn or punctured. The glove design is based on double-dipping between Natural Rubber Latex (NRL) and an inner layer of latex mixed with curcumin, which results in a notable bright yellow-green emission when exposed to UV light. Curcumin (Cur) is a phenolic chemical found primarily in turmeric that fluoresces yellowish-green at 525 nm. The tear region on the glove will glow, indicating the presence of a Cur coating/dipping layer beneath. NRL film is modified by dipping it in a Cur dispersion solution mixed with NRL for the second dipping layer. Using Cur as a filler in NRL also has the distinct advantage of allowing the glove to be made stronger by evenly distributing it throughout the rubber phase. Herein, the optimized design is fully characterized, including physicochemical (fluorescence emission) and mechanical (tensile and tear tests) properties, highlighting the clear potential of this novel and low-cost approach for in situ torn glove detection.
ABSTRACT
Systematic disinfection of the stethoscope diaphragm is required to ensure that it does not act as a vector for cross-transmission of health-related diseases. Thus, an antimicrobial latex film could be used as a cover to inhibit pathogenic bacteria from growing on its surface. The aim of this work is to determine the antimicrobial activity and mechanical properties of antimicrobial natural rubber (NR) latex films with different types of antimicrobial agents (mangosteen peel powder (MPP), zinc oxide nanoparticles (ZnO NP), and povidone-iodine (PVP-I)). The antimicrobial loading was varied from 0.5, to 1.0, and 2.0 phr to monitor the effective inhibition of Gram-negative bacteria and fungi growth. For MPP and PVP-I antimicrobial agents, a loading of 2.0 phr showed good antimicrobial efficacy with the largest zone of inhibition. Simultaneously, ZnO NP demonstrated excellent antimicrobial activity at low concentrations. The addition of antimicrobial agents shows a comparable effect on the mechanical properties of NR latex films. In comparison to control NR latex film (29.41 MPa, 48.49 N/mm), antimicrobial-filled films have significantly greater tensile and tear strengths (MPP (33.84 MPa, 65.21 N/mm), ZnO NP (31.79 MPa, 52.77 N/mm), and PVP-I (33.25 MPa, 50.75 N/mm). In conclusion, the addition of antimicrobial agents, particularly ZnO NP, can be a better choice for NR latex films because they will serve as both an activator and an antimicrobial. In a clinical context, with regard to frequently used medical equipment such as a stethoscope, such an approach offers significant promise to aid infection control.
ABSTRACT
With increased awareness on the importance of gloves arising from the COVID-19 pandemic, people are expected to continue using them even after the pandemic recedes. This scenario in a way increased the rubber solid waste disposal problem; therefore, the production of biodegradable gloves may be an option to overcome this problem. However, the need to study the shelf life of biodegradable gloves is crucial before commercialization. There are well-established models to address the failure properties of gloves as stated in the American Society for Testing and Material (ASTM) D7160. In this study, polysaccharide-based material-filled natural rubber latex (PFNRL) gloves, which are biodegradable gloves, were subjected to an accelerated aging process at different temperatures of 50-80 °C for 1-120 days. Prediction models based on Arrhenius and shift factors were used to estimate the shelf life of the PFNRL gloves. Based on the results obtained, the estimated time for the PFNRL gloves to retain 75% of their tensile strength at shelf temperature (30 °C) based on Arrhenius and shift factor models was 2.8 years. Verification on the activation energy based on the shift factor model indicated that the shelf life of PFNRL gloves is 2.9 years, which is only a 3.6% difference. The value obtained is aligned with the requirement in accordance with ASTM D7160, which states that only up to a maximum of 3 years' shelf life is allowed for the gloves under accelerated aging conditions.