In situ synchrotron x-ray diffraction studies monitoring mechanochemical reactions of hard materials: Challenges and limitations.

In situ monitoring of mechanochemical reactions of soft matter is feasible by synchrotron diffraction experiments. However, so far, reactions of hard materials in existing polymer milling vessels failed due to insufficient energy input. In this study, we present the development of a suitable setup for in situ diffraction experiments at a synchrotron facility. The mechanochemical transformation of boehmite, γ-AlOOH, to corundum, α-Al2O3, was chosen as a model system. The modifications of the mill's clamping system and the vessels themselves were investigated separately. Starting from a commercially available Retsch MM 400 shaker mill, the influence of the geometrical adaptation of the setup on the milling process was investigated. Simply extending the specimen holder proved to be not sufficient because changes in mechanical forces need to be accounted for in the construction of optimized extensions. Milling vessels that are suitable for diffraction experiments and also guarantee the required energy input as well as mechanical stability were developed. The vessels consist of a steel body and modular polymer/steel rings as x-ray transparent windows. In addition, the vessels are equipped with a gas inlet and outlet system that is connectable to a gas analytics setup. Based on the respective modifications, the transformation of boehmite to corundum could be observed in an optimized setup.

In Situ Synchrotron X-ray Diffraction Studies of the Mechanochemical Synthesis of ZnS from its Elements.

Invited for the cover of this issue is Claudia Weidenthaler and co-workers at the Max-Planck-Institut für Kohlenforschung, Shenzhen University and Deutsches Elektronen Synchrotron. The image depicts the X-ray diffraction results showing the formation of ZnS and the subsequent phase transition from the hexagonal to the cubic modification. Read the full text of the article at 10.1002/chem.202101260.

In Situ Synchrotron X-ray Diffraction Studies of the Mechanochemical Synthesis of ZnS from its Elements.

Mechanochemistry, as a synthesis tool for inorganic materials, became an ever-growing field in material chemistry. The direct energy transfer by collision of the educts with the milling media gives the possibility to design environmental-friendly reactions. Nevertheless, the underlying process of energy transfer and hence the kinetics of mechanosynthesis remain unclear. Herein, we present in situ synchrotron X-ray diffraction studies coupled with pressure measurements performed during the formation of ZnS and the subsequent phase transition (PT) from the hexagonal to the cubic modification. Milling Zn and S8 results in the sublimation of S8 , observed by a sudden pressure increase. Simultaneously, the hexagonal metastable ZnS-modification (wurtzite) forms. Via detection of the pressure maximum, the exact start of the wurtzite formation can be determined. Immediately after the formation of wurtzite, the structural PT to the thermodynamic stable cubic modification sphalerite takes place. This PT can be described by the Prout-Tompkins equation for autocatalytic reactions, similar to thermally induced PT in sulfur vapor at high temperatures (T>1133 K). The increase in the reactivity of the wurtzite formation is explained by the reaction in sulfur vapor and the induction of defect structures by the collisions with the milling media.