Reduced Graphene Oxide-Silver Nanoparticles for Optical Pulse Generation in Ytterbium- and Erbium-Doped Fiber Lasers.

This work has demonstrated the potential of a reduced graphene oxide silver/polyvinyl alcohol (rGO-Ag/PVA) film as a saturable absorber (SA) in ytterbium and erbium based Q-switched optical fiber lasers. The facile hydrothermal method was used to synthesize the nanocomposite between rGO and Ag nanoparticles. This was followed by a simple solution method to form the rGO-Ag film using PVA as the host polymer. From nonlinear absorption characterization, the rGO-Ag/PVA SA was determined to have a modulation depth of 30%, a nonsaturable loss of 70%, and a saturable intensity of 0.63 kW/cm2. Stable self-starting Q-switched pulses were obtained at the threshold pump power of 72.76 mW and 18.63 mW in the ytterbium-doped (YDFL) and erbium-doped fiber laser (EDFL) cavities respectively. The center operating wavelengths were observed at 1044.4 nm and 1560 nm for the two cavities. The shortest pulse width and maximum repetition rate of the YDFL and EDFL were 1.10 µs and 62.10 kHz and 1.38 µs and 76.63 kHz respectively. This work has demonstrated that the rGO-Ag/PVA film is suitable as an SA for pulse generation in the 1.0 and 1.5 µm regions and would have many potential photonics applications.

Chitosan capped nickel oxide nanoparticles as a saturable absorber in a tunable passively Q-switched erbium doped fiber laser.

Nickel oxide (NiO) nanoparticles successfully prepared from a nickel(ii) chloride hexahydrate precursor are used to form a chitosan capped NiO nanoparticle thin film to serve as a saturable absorber (SA) for the generation of passively Q-switched pulses in an erbium doped fiber laser (EDFL). The NiO/chitosan SA based EDFL is able to generate stable pulsed outputs at a low threshold pump power of 104.90 mW with a central wavelength at 1562 nm. The highest pulse energy obtainable by the system is 15.30 nJ at a repetition rate of 42.66 kHz and a pulse duration of 2.02 µs. The laser has a spectral range of 58 nm from 1522 to 1580 nm, covering the C and L bands and even portions of the S band. This study experimentally demonstrates that the potential of the NiO/chitosan film as an SA material for Q-switching operations, combined with the biocompatibility, non-toxicity and high thermal resistance of Chitosan, holds great prospects for a broad range of applications.