ABSTRACT
The inadequate management of organic waste and excessive use of plastic containers cause damage to the environment; therefore, different studies have been carried out to obtain new biomaterials from agricultural subproducts. The objective of this work was to evaluate the feasibility of using the pectin extracted from the peel of Passiflora tripartita var. mollissima (PT), characterizing its type and viability for the production of edible biodegradable films. In addition, films of two thicknesses (23.45 ± 3.02 µm and 53.34 ± 2.28 µm) were prepared. The results indicated that PT is an excellent raw material for the extraction of pectin, with high yields (23.02 ± 0.02%), high galacturonic acid content (65.43 ± 2.241%), neutral sugars (ribose, xylose, glucose) and a high degree of esterification (76.93 ± 1.65%), classifying it as a high-methoxy pectin. Regarding the films, they were malleable and flexible, with a water vapor permeability from 2.57 × 10-10 ± 0.046 to 0.13 × 10-10 ± 0.029 g/s mPa according to thickness, being similar to other Passiflora varieties of edible films. The pectin extraction yield from PT makes this fruit a promising material for pectin production and its chemical composition a valuable additive for the food and pharmaceutical industries.
ABSTRACT
Valorization of by-products obtained from food processing has achieved an important environmental impact. In this research, sunflower wax recovered from oil refining process was incorporated to low and high-methoxyl pectin films produced by electrospraying. Film-forming solutions and wax-added electrosprayed films were physical and structurally evaluated. The addition of sunflower wax to the film-forming solutions reduces conductivity while raising surface tension and density, whereas the type of pectin had a larger impact on viscosity, with the low-methoxyl solution having the highest value. These changes in physical solution properties influenced the film characteristics, observing thicker films with lower water vapor transmission rate (WVTR) when adding wax. Micrographs obtained by scanning electron microscopy (SEM) revealed the presence of wax particles as small spherical shapes, having a good distribution through the sectional area of films. According to X-ray diffraction (XRD), atomic force microscopy (AFM) and mechanical properties analyses, the presence of wax had an impact on the degree of crystallinity, producing a more amorphous and rougher film's structure, without affecting the elongation percentage and the tensile stress (p>0.05). These results showed that wax addition improves the physical properties of films, while the suitability of using both pectins and the electrospraying technique was demonstrated.
ABSTRACT
Biological, physicochemical, structural, and thermal properties of PVA-based electrospun wound dressings added with hydrolyzed collagen (HC) and different concentrations of Hypericum perforatum ethanolic extract (EEHP) were studied. Membrane characterization was carried out by X-ray diffraction, Fourier infrared spectroscopy, differential scanning calorimetry, barrier properties, scanning electron microscopy, image analysis (diameter and pore size), as well as antimicrobial and anti-inflammatory activities. Results showed that the PVA/HC/EEHP materials, fabricated under controlled conditions of temperature and humidity, generated fiber membranes with diameters between 140−390 nm, adequate porosity and pore size for cell growth (67−90% and 4−16 µm, respectively), and good barrier properties (0.005−0.032 g·m−2 s−1) to be used in the treatment of conditions on the skin, and was even better than some commercial products. Finally, they showed to have anti-inflammatory (>80%), and antimicrobial activity against S. aureus and S. epiderm. Furthermore, higher crystalline structure was observed according to the EEHP concentration. In addition, this is the first report in which PVA/HC/EEHP membranes are successfully fabricated and characterized.