ABSTRACT
Peak external quantum efficiencies (EQEs) of just over 120% were observed in photovoltaic (PV) devices of CuInSe2 nanocrystals prepared with a photonic curing process. The extraction of more than one electron/hole pair as a result of the absorption of a single photon can occur if multiple excitons are generated and extracted. Multiexciton generation (MEG) in the nanocrystal films was substantiated by transient absorption spectroscopy. We propose that photonic curing leads to sufficient electronic coupling between nanocrystals to enable multiexciton extraction under typical solar illumination conditions. Under low light conditions, however, the EQE drops significantly, indicating that photonic curing-induced ligand desorption creates a significant amount of traps in the film that limit the overall power conversion efficiency of the device.
ABSTRACT
CuInSe2 (CISe) quantum dots (QDs) were synthesized with tunable size from less than 2 to 7 nm diameter. Nanocrystals were made using a secondary phosphine selenide as the Se source, which, compared to tertiary phosphine selenide precursors, was found to provide higher product yields and smaller nanocrystals that elicit quantum confinement with a size-dependent optical gap. Photovoltaic devices fabricated from spray-cast CISe QD films exhibited large, size-dependent, open-circuit voltages, up to 849 mV for absorber films with a 1.46 eV optical gap, suggesting that midgap trapping does not dominate the performance of these CISe QD solar cells.