Effect of four different mono and multi-wave light-curing units on the Knoop hardness of veneer resin composites.

OBJECTIVES: To evaluate the effect of mono and multi-wave light-curing units (LCUs) on the Knoop hardness of resin-based composites (RBC) that use different photoinitiators. METHODS: Central incisor-shaped specimens 12 mm long, 9 mm wide, and 1.5 mm thick were made from 2 RBCs that use different photoinitiators: Tetric N-Ceram (Ivoclar Vivadent) - and Vittra APS (FGM), both A2E shade. They were light-cured with 4 different LCUs: two claimed to be multi-wave - VALO Grand (Ultradent) and Emitter Now Duo (Schuster); and two were monowave - Radii Xpert (SDI) and Elipar DeepCure-L (3 M Oral Care) using 2 different light exposure protocols: one 40 s exposure centered over the specimen; and two 20 s light exposures that delivered light from two positions to better cover the entire tooth. 16 groups with 10 specimens in each group were made. The Knoop hardness (KH, kg/mm2) was measured at the top and bottom of the specimen in the center and at the cervical, incisal, mesial, and distal peripheral regions. The active tip diameters (mm) and spectral radiant powers (mW/nm) of the LCUs were measured with and without the interposition of the RBC, as well as the radiant exposure beam profiles (J/cm²) delivered to the top of the RBCs. The data was analyzed using Three-way ANOVA and Tukey's tests (α = 0.05). RESULTS: The VALO Grand (1029 mW) emitted twice the power of the Radii Xpert (500 mW). The KH values of VI and TN resin composite specimens were significantly affected by the LCU used (p < .001), the measurement location (p < .001), and the surface of the specimen (p < .001). LCUs with wider tip diameters produced greater Knoop hardness values at the peripheries of the 12 mm of long, 9 mm wide specimens. In general, the VALO Grand produced the highest KH values, followed by Elipar DeepCure-L, then by Radii Xpert. The Emitter Now Duo LCU produced the lowest values. Exposing the veneers from two locations reduced the differences between the LCUs and the effect of the measurement location. Only the VALO Grand could fully cover the composite veneer with light when the two locations were used. SIGNIFICANCE: The light tip must cover the entire restoration to photocure the RBC beneath the light tip.

Effect of thickness and shade of CAD/CAM composite on the light transmission from different light-curing units.

The thickness and shade of a restoration will affect the transmission of light from the light-curing unit (LCU). This study determined the power (mW), spectral radiant power (mW/nm), and beam profile of different LCUs through various thicknesses and shades of a CAD-CAM resin composite (BRAVA Block, FGM). Five thicknesses: 0.5; 0.75; 1.0; 1.5, and 2.0 mm, in three shades: Bleach; A2 and A3.5 of a CAD-CAM resin (n = 5). Two single-peak LCUs: EL, Elipar DeepCure-S (3M Oral Care); and OP, Optilight Max (Gnatus), and one multiple-peak LCU: VL, VALO Grand (Ultradent), were used. The LCUs were positioned touching the surface of the BRAVA Block. The power and emission spectrum were measured using a fiberoptic spectrometer attached to an integrating sphere, and the beam profiles using a laser beam profiler. The effect of the material thickness on the light attenuation coefficients was determined. VL and EL delivered more homogeneous beam profiles than OP. The type of the BRAVA Block had a significant effect on the transmitted power, and wavelengths of transmitted light (p < 0.001). There was an exponential reduction in the power and emission spectrum as the thickness of the BRAVA Block increased (p < 0.001). The light transmission through the A2 shade was least affected by the thickness (p < 0.001). The attenuation coefficient was higher for the violet light and higher for A3.5 than the A2 or Bleach shades. No violet light from the VL could be detected at the bottom of 2.0 mm of the BRAVA Block.

Survival of severely compromised endodontically treated teeth restored with or without a fiber glass post.

OBJECTIVE: The use of a fiber glass post (FGP) type and choice of FGP diameter to restore endodontically treated incisors without ferrule is controversial. This study evaluated survival rate and failure mode of severely compromised central incisors without ferrule rehabilitated using resin-based composite (RBC) with or without FGP with different diameters. METHODOLOGY: A total of 60 decoronated bovine incisors without a ferrule were endodontically treated and prepared for 1.4, 1.6, and 1.8 mm diameter FGPs (Whitepost System DC 0.5, Fit 0.4, and DCE 0.5; FGM). Half of the teeth received FGPs cemented using dual-cure resin cement (Allcem Core; FGM), the other half were filled using only bulk-fill RBC (OPUS Bulk Fill; FGM). The crowns were directly restored with RBC. The roots were embedded in polystyrene resin and the periodontal ligament was simulated with polyether impression material. Fatigue testing was conducted under 5 Hz cyclic loading at 30 degrees to the incisal edge, beginning at 50 N (5,000 cycles) as a warmup. After, the load was increased 100 N every 15,000 cycles until fracture occurred. All specimens were subjected to transillumination, micro-CT analysis, and digital radiography before and after fatigue testing. Fracture mode was classified according to severity and repair potential. Data were analyzed with Kaplan-Meier survival test and post hoc log-rank test (α=0.05) for pairwise comparisons. RESULTS: Using FGP significantly increased the number of cycles to failure, irrespective of FGP diameters (p=0.001). The FGP diameters had no statistically significant effect on cycles to failure or failure mode. CONCLUSION: Using FGP without ferrule improved survival rate of structurally severely compromised central incisors compared with rehabilitation without FGP. The diameter of the FGPs had no effect on the survival rate and failure mode.

Effects of different calcium-silicate based materials on fracture resistance of immature permanent teeth with replacement root resorption and osteoclastogenesis.

Objectives: This study evaluated the effects of Biodentine (BD), Bio-C Repair (BCR), and mineral trioxide aggregate (MTA) plug on the fracture resistance of simulated immature teeth with replacement root resorption (RRR) and in vitro-induced osteoclastogenesis. Materials and Methods: Sixty bovine incisors simulating immature teeth and RRR were divided into 5 groups: BD and BCR groups, with samples completely filled with the respective materials; MTA group, which utilized a 3-mm apical MTA plug; RRR group, which received no root canal filling; and normal periodontal ligament (PL) group, which had no RRR and no root canal filling. All the teeth underwent cycling loading, and compression strength testing was performed using a universal testing machine. RAW 264.7 macrophages were treated with 1:16 extracts of BD, BCR, and MTA containing receptor activator of nuclear factor-kappa B ligand (RANKL) for 5 days. RANKL-induced osteoclast differentiation was assessed by staining with tartrate-resistant acid phosphatase. The fracture load and osteoclast number were analyzed using 1-way ANOVA and Tukey's test (α = 0.05). Results: No significant difference in fracture resistance was observed among the groups (p > 0.05). All materials similarly inhibited osteoclastogenesis (p > 0.05), except for BCR, which led to a lower percentage of osteoclasts than did MTA (p < 0.0001). Conclusions: The treatment options for non-vital immature teeth with RRR did not strengthen the teeth and promoted a similar resistance to fractures in all cases. BD, MTA, and BCR showed inhibitory effects on osteoclast differentiation, with BCR yielding improved results compared to the other materials.

Effect of surface treatment of ethylene vinyl acetate on the delamination of custom-fitted mouthguards.

BACKGROUND/AIM: Contamination of ethylene vinyl acetate (EVA) during mouthguard fabrication can cause delamination. The study evaluated the effects of different EVA surface treatments on the contact angle, laminate bond strength, and elongation capacity. MATERIALS AND METHODS: Specimens of two bonded EVA plates were prepared (n = 30). The Shore A hardness of standardized EVA plate specimens was measured before and after thermo-plasticization. The EVA plates were randomly allocated to one of five different surface treatment groups: no treatment (control); isopropyl alcohol, 100%; chloroform, 99.8%; self-cure acrylic resin monomer (methacrylate, ethylene glycol dimethacrylate, and chemical initiator-amine type); and ethyl alcohol, 70%. The maximum breaking force and elongation at the site of fracture were recorded using a universal testing machine. The contact angle surface was measured using ImageJ software. Scanning electron microscopy of the EVA surface was performed. The laminate bond strength was obtained by dividing the maximum breaking force by the bonding area between the two EVA plates. The laminate bond strength and maximum elongation data were analyzed by one-way ANOVA, followed by the Tukey's and the Dunnet test. The failure mode data was analyzed using the chi-square test (α = .05). RESULTS: EVA surface treatment significantly influenced the laminate bond strength and maximum elongation (p < .001). The control group had a higher contact angle and significantly lower laminate bond strength and maximum elongation than the other groups (p < .001). The acrylic resin monomer and chloroform-treated specimens had similar laminate bond strength and maximum elongation. The acrylic resin monomer group had a significantly lower contact angle (p < .001). CONCLUSIONS: All treatments had a significantly higher laminate bond strength and maximum elongation than the control group. The acrylic resin monomer and chloroform groups had a significantly higher laminate bond strength and maximum elongation and the acrylic resin monomer group had a lower contact angle than the other groups. The chloroform should be avoided due its hazardous effects.

Effect of thickness and shade of CAD/CAM composite on the light transmission from different light-curing units

Abstract The thickness and shade of a restoration will affect the transmission of light from the light-curing unit (LCU). This study determined the power (mW), spectral radiant power (mW/nm), and beam profile of different LCUs through various thicknesses and shades of a CAD-CAM resin composite (BRAVA Block, FGM). Five thicknesses: 0.5; 0.75; 1.0; 1.5, and 2.0 mm, in three shades: Bleach; A2 and A3.5 of a CAD-CAM resin (n = 5). Two single-peak LCUs: EL, Elipar DeepCure-S (3M Oral Care); and OP, Optilight Max (Gnatus), and one multiple-peak LCU: VL, VALO Grand (Ultradent), were used. The LCUs were positioned touching the surface of the BRAVA Block. The power and emission spectrum were measured using a fiberoptic spectrometer attached to an integrating sphere, and the beam profiles using a laser beam profiler. The effect of the material thickness on the light attenuation coefficients was determined. VL and EL delivered more homogeneous beam profiles than OP. The type of the BRAVA Block had a significant effect on the transmitted power, and wavelengths of transmitted light (p < 0.001). There was an exponential reduction in the power and emission spectrum as the thickness of the BRAVA Block increased (p < 0.001). The light transmission through the A2 shade was least affected by the thickness (p < 0.001). The attenuation coefficient was higher for the violet light and higher for A3.5 than the A2 or Bleach shades. No violet light from the VL could be detected at the bottom of 2.0 mm of the BRAVA Block.

Survival of severely compromised endodontically treated teeth restored with or without a fiber glass post

Abstract Objective The use of a fiber glass post (FGP) type and choice of FGP diameter to restore endodontically treated incisors without ferrule is controversial. This study evaluated survival rate and failure mode of severely compromised central incisors without ferrule rehabilitated using resin-based composite (RBC) with or without FGP with different diameters. Methodology A total of 60 decoronated bovine incisors without a ferrule were endodontically treated and prepared for 1.4, 1.6, and 1.8 mm diameter FGPs (Whitepost System DC 0.5, Fit 0.4, and DCE 0.5; FGM). Half of the teeth received FGPs cemented using dual-cure resin cement (Allcem Core; FGM), the other half were filled using only bulk-fill RBC (OPUS Bulk Fill; FGM). The crowns were directly restored with RBC. The roots were embedded in polystyrene resin and the periodontal ligament was simulated with polyether impression material. Fatigue testing was conducted under 5 Hz cyclic loading at 30 degrees to the incisal edge, beginning at 50 N (5,000 cycles) as a warmup. After, the load was increased 100 N every 15,000 cycles until fracture occurred. All specimens were subjected to transillumination, micro-CT analysis, and digital radiography before and after fatigue testing. Fracture mode was classified according to severity and repair potential. Data were analyzed with Kaplan-Meier survival test and post hoc log-rank test (α=0.05) for pairwise comparisons. Results Using FGP significantly increased the number of cycles to failure, irrespective of FGP diameters (p=0.001). The FGP diameters had no statistically significant effect on cycles to failure or failure mode. Conclusion Using FGP without ferrule improved survival rate of structurally severely compromised central incisors compared with rehabilitation without FGP. The diameter of the FGPs had no effect on the survival rate and failure mode.

Effect of Light-curing Unit Design and Mouth Opening on the Polymerization of Bulk-fill Resin-based Composite Restorations in Molars.

PURPOSE: This study evaluated the effect of the design of the light-curing unit (LCU) and mouth opening on the properties of bulk-fill resin-based composites (RBCs). MATERIALS AND METHODS: Eighty molars received a mesio-occlusal-distal preparation and were restored using two different bulk-fill RBCs, Opus Bulk Fill APS (FGM) and Filtek Bulk Fill One (3M Oral Care), using two different designs of LCU, straight (Valo Cordless [Ultradent]) and angled (Radii-Cal [SDI]). Two mouth openings of 25 and 45 mm at the incisors were used. Forty samples were sectioned mesiodistally. One half was immersed in tetrahydrofuran to examine the effect of the solvent on the RBCs (SE), and the other half to measure the degree of conversion (DC) in proximal and occlusal boxes using Fourier Transform Infrared spectroscopy. The other 40 samples were subjected to thermomechanical fatigue and immersed in silver nitrate to examine the gingival margin integrity (GMI) using SEM. The irradiance (mW/cm2) and emission spectrum (mW/cm2/nm) from the LCUs were measured using a MARC Resin Calibrator (BlueLight Analytics). DC data were analyzed by 3-way ANOVA and Tukey's test; SE and GMI were analyzed by an ANOVA on Ranks and Dunn test (α = 0.05). RESULTS: The DC values were similar in the occlusal and proximal boxes when using Valo Cordless, irrespective of RBC and the mouth opening used. Lower DC values were measured in proximal boxes when using Radii-Cal. The mouth opening had a greater effect on the irradiance delivered by Radii-Cal. Radii-Cal with 25-mm mouth opening had greater SE and GMI values, whereas the SE and GMI values obtained with Valo Cordless were unaffected by mouth opening. CONCLUSION: The choice of LCU did not influence the properties of tested bulk-fill RBCs when the 45-mm mouth opening was used. However, when using the 25-mm mouth opening, the choice of LCU did influence the properties of the RBCs.

Effect of infection control barriers on the light output from a multi-peak light curing unit.

OBJECTIVES: Curing lights cannot be sterilized and should be covered with an infection control barrier. This study evaluated the effect of barriers when applied correctly and incorrectly on the radiant power (mW), irradiance (mW/cm2), emission spectrum (mW/nm), and beam profile from a multi-peak light-curing unit (LCU). METHODS: Five plastic barriers (VALO Grand, Ultradent; TIDIShield, TIDI Products; Disposa-Shield, Dentsply Sirona; Cure Sleeve, Kerr; Stretch and Seal, Betty Crocker) and one latex-based barrier (Curelastic, Steri-Shield) were tested. The radiant power (mW) and emission spectrum (mW/nm) from one multi-peak LCU (VALO Grand, Ultradent) was measured using an integrating sphere. LCU tip internal diameter (mm) was measured, then the tip area and irradiance (mW/cm2) were calculated. The beam profiles were measured using a laser beam profiler. RESULTS: When applied correctly, the plastic barriers reduced the radiant power output by 5-8%, and the latex-based barrier by 16%. When the plastic seam or barrier opaque face was positioned over the LCU tip, the power output was reduced by 8-11%. When the plastic barriers were wrinkled, the power output was significantly reduced by 14-26%. The wrinkled latex-based barrier reduced by 28%, and further reduced the violet light. The beam profiles illustrated the importance of correctly barrier use without wrinkles over the tip. CONCLUSIONS: Plastic barriers applied correctly reduced the light output (mW) by 5-8%. The barriers applied incorrectly significantly reduced the light output by 14-26%. The latex-based barrier wrinkled also reduced the amount of violet light. CLINICAL RELEVANCE: Infection control curing light barriers should be used to prevent cross-infection between patients. However, they must be applied correctly to reduce their negative effects on the light output.

Molar cusp deformation evaluated by micro-CT and enamel crack formation to compare incremental and bulk-filling techniques.

OBJECTIVES: To describe a method of measuring the molar cusp deformation using micro-computed tomography (micro-CT), the propagation of enamel cracks using transillumination, and the effects of hygroscopic expansion after incremental and bulk-filling resin composite restorations. METHODS: Twenty human molars received standardized Class II mesio-occlusal-distal cavity preparations. They were restored with either a bulk-fill resin composite, X-tra fil (XTRA), or a conventional resin composite, Filtek Z100 (Z100). The resin composites were tested for post-gel shrinkage using a strain gauge method. Cusp deformation (CD) was evaluated using the images obtained using a micro-CT protocol and using a strain-gauge method. Enamel cracks were detected using transillumination. RESULTS: The post-gel shrinkage of Z100 was higher than XTRA (P < 0.001). The amount of cusp deformation produced using Z100 was higher compared to XTRA, irrespective of the measurement method used (P < 0.001). The thinner lingual cusp always had a higher CD than the buccal cusp, irrespective of the measurement method (P < 0.001). A positive correlation (r = 0.78) was found between cusp deformation measured by micro-CT or by the strain-gauge method. After hygroscopic expansion of the resin composite, the cusp displacement recovered around 85% (P < 0.001). After restoration, Z100 produced more cracks than XTRA (P = 0.012). CONCLUSIONS: Micro-CT was an effective method for evaluating the cusp deformation. Transillumination was effective for detecting enamel cracks. There were fewer negative effects of polymerization shrinkage in bulk-fill resin restorations using XTRA than for the conventional incremental filling technique using conventional composite resin Z100. CLINICAL SIGNIFICANCE: Shrinkage and cusp deformation are directly related to the formation of enamel cracks. Cusp deformation and crack propagation may increase the risk of tooth fracture.