ABSTRACT
Silicon wafers are commonly etched in potassium hydroxide solutions to form highly symmetric surface structures. These arise when slow-etching {111} atomic planes are exposed on standard low-index surfaces. However, the ability of nonstandard high-index wafers to provide more complex structures by tilting the {111} planes has not been fully appreciated. We demonstrate the power of this approach by creating chiral surface structures and nanoparticles of a specific handedness from gold. When the nanoparticles are dispersed in liquids, gold colloids exhibiting record molar circular dichroism (>5 × 10(9) M(-1) cm(-1)) at red wavelengths are obtained. The nanoparticles also present chiral pockets for binding.
ABSTRACT
The application of focused ion beam (FIB) nanotomography and Rutherford backscattering spectroscopy (RBS) to dealloyed platinum-aluminum thin films allows for an in-depth analysis of the dominating physical mechanisms of nanoporosity formation during the dealloying process. The porosity formation due to the dissolution of the less noble aluminum in the alloy is treated as result of a reaction-diffusion system. The RBS and FIB analysis yields that the porosity evolution has to be regarded as superposition of two independent processes, a linearly propagating diffusion front with a uniform speed and a slower dissolution process in regions which have already been passed by the diffusion front. The experimentally observed front evolution is captured by the Fisher-Kolmogorov-Petrovskii-Piskounov (FKPP). The slower dissolution is represented by a zero-order rate law which causes a gradual porosity in the thin film.