Fiber Spinning of Ultrahigh Molecular Weight Isotactic Polypropylene: Melt Spinning and Melt Drawing.

Herein, this work reports fiber spinning of tailored isotactic polypropylene (iPP) by melt spinning and melt drawing, yielding an adjustable diameter of 40-400 µm. The crystallinity of all obtained fibers with a molecular weight between 330-1400 kg/mol is increased by thermal annealing and investigated via differential scanning calorimetry (DSC) as well as wide angle X-ray scattering (WAXS). The potential of ultrahigh molecular weight iPP (UHMW-iPP) fibers compared to fibers manufactured from industrially available iPP becomes evident when the mechanical performance is compared: fibers spun from UHMW-iPP (1400 kg/mol) enable a tensile strength of up to 400 MPa, whereas commercially available fibers (330 kg/mol) show a tensile strength of approximately 50 MPa. However, UHMW-iPP exhibits a short timeframe, in which extrusion is possible, thereafter extrusion rupture occurs, probably induced by an increased melt viscosity.

Defect Creation in Surface-Mounted Metal-Organic Framework Thin Films.

Defect engineering is a strategy for tailoring the properties of metal-organic frameworks (MOFs). Plenty of efforts have been devoted to study the defect chemistry and structures of bulk MOFs; however, the reported example of a defect-engineered surface-mounted MOF (SURMOF) thin film is rare. In this work, defects were incorporated in SURMOF thin films by using defect-generating linkers and taking advantage of the liquid-phase stepwise epitaxial layer-by-layer growth (LBL). Two methods based on the LBL, named mixing method and alternating method, are proposed for incorporating defects in the prototypical SURMOF HKUST-1 by partially substituting the parent H3btc (benzene-1,3,5-tricarboxylic acid) linker with a set of defect-generating linkers H2ip (isophthalic acid), H2OH-ip (5-hydroxyisophthalic acid), and H2pydc (3,5-pyridinedicarboxylic acid). The crystallinity and phase purity of the obtained "defected" SURMOFs were confirmed by X-ray diffraction, infrared reflection absorption spectroscopy, and Raman spectroscopy. The incorporation of the defect-generating linkers and the types of induced defects were characterized by ultraviolet-visible spectroscopy, time-of-flight secondary ion mass spectrometry, methanol adsorption, scanning electron microscopy, and 1H nuclear magnetic resonance spectroscopy (after digestion of the samples). These two methods provide avenues for controlling the defect formation in MOF thin films.

Unprecedented High Oxygen Evolution Activity of Electrocatalysts Derived from Surface-Mounted Metal-Organic Frameworks.

The oxygen evolution reaction (OER) is a key process for renewable energy storage. However, developing non-noble metal OER electrocatalysts with high activity, long durability and scalability remains a major challenge. Herein, high OER activity and stability in alkaline solution were discovered for mixed nickel/cobalt hydroxide electrocatalysts, which were derived in one-step procedure from oriented surface-mounted metal-organic framework (SURMOF) thin films that had been directly grown layer-by-layer on macro- and microelectrode substrates. The obtained mass activity of ∼2.5 mA·µg-1 at the defined overpotential of 300 mV is 1 order of magnitude higher than that of the benchmarked IrO2 electrocatalyst and at least 3.5 times higher than the mass activity of any state-of-the-art NiFe-, FeCoW-, or NiCo-based electrocatalysts reported in the literature. The excellent morphology of the SURMOF-derived ultrathin electrocatalyst coating led to a high exposure of the most active Ni- and Co-based sites.

Superhydrophobic Silicon Nanocrystal-Silica Aerogel Hybrid Materials: Synthesis, Properties, and Sensing Application.

Silicon nanocrystals (SiNCs) are abundant and exhibit exquisitely tailorable optoelectronic properties. The incorporation of SiNCs into highly porous and lightweight substrates such as aerogels leads to hybrid materials possessing the attractive features of both materials. This study describes the covalent deposition of SiNCs on and intercalation into silica aerogels, explores the properties, and demonstrates a prototype sensing application of the composite material. SiNCs of different sizes were functionalized with triethoxyvinylsilane (TEVS) via a radical grafting approach and subsequently used for the synthesis of photoluminescent silica hybrids. The resulting SiNC-containing aerogels possess high porosities, SiNC-based size-dependent photoluminescence, transparency, and a superhydrophobic macroscopic surface. The materials were used to examine the photoluminescence response toward low concentrations of 3-nitrotoluene (270 µM), demonstrating their potential as a sensing platform for high-energy materials.