Corrosion Inhibition in CO2-Saturated Brine by Nd3+ Ions.

This study reports the use of an inorganic corrosion inhibitor to mitigate dissolved CO2-induced corrosion. Using electrochemical techniques (polarization curves, open circuit potential, polarization resistance, and electrochemical impedance), the effect of adding Nd3+ ions on the corrosion resistance of X52 steel immersed in CO2-saturated brine at 20 °C and 60 °C was evaluated. The polarization curves showed that the Icorr values tend to decrease with increasing Nd3+ ion concentration, up to the optimal inhibition concentration, and that the corrosion potential increases at nobler values. Open circuit potential measurements showed a large increase in potential values immediately after the addition of the Nd3+ ions. Similarly, polarization resistance measurements showed similar trends. It was observed that regardless of temperature, Nd3+ ions can reduce the corrosion rate by more than 97% at doses as low as 0.001 M. Electrochemical impedance measurements confirmed the formation of a protective layer on the steel surface, which caused an increase in the magnitude of the impedance module and phase angle, which indicates an increase in the resistance to charge transfer and capacitive properties of the metallic surface. The characterization of the metallic surface showed that the protective layer was formed by Nd carbonates, whose formation was due to a CO2 capture process.

Behavior of Ni20Cr Alloy in Molten Nitrate Salts.

This study reports the behavior of the Ni20Cr alloy in molten nitrate salts. Its behavior was evaluated in the eutectic mixture called Solar Salt (binary salt) and in a ternary mixture (90% Solar Salt and 10% lanthanum nitrate). The addition of lanthanum nitrate was performed to determine if the presence of the La3+ cation could act as a corrosion inhibitor. Through mass loss and potentiodynamic polarization studies, the effects of both electrolytes on the corrosion resistance of the alloy at 300, 400, and 500 °C and at exposure times of 250, 500, 750, and 1000 h were determined. The results showed an increase in the corrosivity of the ternary salt, due to a decrease in its melting point and an increase in the concentration of nitrate ions. However, it was observed that the La3+ cations formed a protective layer (La2O3) on the alloy surface. In both corrosive media, the Ni20Cr alloy showed excellent corrosion resistance, due to its ability to form protective layers of Cr2O3, NiO, and NiCr2O4, in addition to the presence of a layer of La2O3 in the case of the ternary salt.

Corrosion Behavior of Al Modified with Zn in Chloride Solution.

Aluminum-based alloys have been considered candidate materials for cathodic protection anodes. However, the Al-based alloys can form a layer of alumina, which is a drawback in a sacrificial anode. The anodes must exhibit uniform corrosion to achieve better performance. Aluminum can be alloyed with Zn to improve their performance. In this sense, in the present research, the electrochemical corrosion performance of Al-xZn alloys (x = 1.5, 3.5, and 5 at.% Zn) exposed to 3.5 wt.% NaCl for 24 h was evaluated. Polarization curves, linear polarization resistance (LPR), and electrochemical impedance spectroscopy (EIS) were used to identify the electrochemical behavior. The microstructure of the samples before the corrosion assessment was characterized by means of X-ray diffraction analyses (XRD) and scanning electron microscopy (SEM). In addition, microstructures of the corroded surfaces were characterized using X-ray mappings via SEM. Polarization curves indicated that Zn additions changed the pseudo-passivation behavior from what pure Al exhibited in a uniform dissolution regime. Furthermore, the addition of Zn shifted the corrosion potential to the active side and increased the corrosion rate. This behavior was consistent with the proportional decrease in polarization resistance (Rp) and charge transfer resistance (Rct) in the EIS. The analysis of EIS was done using a mathematical model related to an adsorption electrochemical mechanism. The adsorption of chloride at the Al-Zn alloy surface formed aluminum chloride intermediates, which controlled the rate of the process. The rate constants of the reactions of a proposed chemical mechanism were evaluated.

Electrochemical Performance of Fe40Al-X (X = Cr, Ti, Co, Ni) Alloys Exposed to Artificial Saliva.

Fe-Al intermetallic compounds have been considered excellent candidates as alternative alloys for various applications in corrosive environments compared to other Fe-based alloys. Their excellent corrosion resistance is due to the development of an Al-based passive layer. The performance of the passive layer can be improved by adding a third alloy element. Therefore, in this study the electrochemical performance of the Fe40Al intermetallic alloy modified by the addition of a third alloy element (Cr, Ti, Co, Ni) is evaluated. The corrosion resistance of intermetallic alloys has been evaluated by electrochemical tests (potentiodynamic polarization curves, and measurements of open circuit potential, linear polarization and electrochemical impedance) in artificial saliva. The performance of intermetallic alloys was compared with that of Ti. The results obtained showed that the addition of Ni and Ti substantially improves the corrosion resistance of the base intermetallic. The corrosion resistance shown is comparable or greater than that shown by Ti. However, the addition of Co reduces the corrosion resistance of the base intermetallic.