Molecularly imprinted polymers (MIPs) as efficient catalytic tools for the oxidative degradation of 4-nonylphenol and its by-products.

Water pollution is a current global concern caused by emerging pollutants like nonylphenol (NP). This endocrine disruptor cannot be efficiently removed with traditional wastewater treatment plants (WTPs). Therefore, this work aimed to evaluate the adsorption influence of molecularly imprinted polymers (MIPs) on the oxidative degradation (ozone and ultraviolet irradiations) of 4-nonylphenol (4-NP) and its by-products as a coadjuvant in WTPs. MIPs were synthesized and characterized; the effect of the degradation rate under system operating conditions was studied by Box-Behnken response surface design of experiments. The variables evaluated were 4-NP concentration, ozone exposure time, pH, and MIP amount. Results show that the MIPs synthesized by co-precipitation and bulk polymerizations obtained the highest retention rates (> 90%). The maximum adsorption capacities for 4-NP were 201.1 mg L-1 and 500 mg L-1, respectively. The degradation percentages under O3 and UV conditions reached 98-100% at 120 s of exposure at different pHs. The degradation products of 4-NP were compounds with carboxylic and ketonic acids, and the MIP adsorption was between 50 and 60%. Our results present the first application of MIPs in oxidation processes for 4-NP, representing starting points for the use of highly selective materials to identify and remove emerging pollutants and their degradation by-products in environmental matrices.

Design and application of molecularly imprinted polymers for adsorption and environmental assessment of anti-inflammatory drugs in wastewater samples.

In this study, a series of molecularly imprinted polymers (MIPs) have been synthesized using separately diclofenac, naproxen, and ibuprofen as templates with three different polymerization approaches. Two functional monomers, methacrylic acid (MAA) and 2-vinylpyridine (2-VP), were tested and ethylene glycol dimethacrylate (EGDMA) was used as crosslinker; also, template-free polymers (NIPs) were synthesized. It was found that the MIP with the highest retention percentage for diclofenac was the one prepared by the emulsion approach and with MAA (98.3%); for naproxen, the one prepared by the bulk polymerization with MAA (99%); and for ibuprofen, the one synthesized by bulk with 2-VP (97.7%). These three MIPs were characterized by scanning electron microscopy, thermogravimetric test, Fourier transform infrared, specific area measurements, and surface charge. It was found that the emulsion method allowed particle size control, while the bulk method gave heterogeneous particles. The three evaluated MIPs exhibited thermal stability up to 300 °C, and it was observed that 2-VP confers greater stability to the material. From the BET analysis, it was demonstrated that the MIPs and NIPs evaluated are mesoporous materials with a pore size between 10 and 20 nm. In addition, the monomer influenced the surface charge of the material, since the MAA conferred an acidic point of zero charge (PZC), while the 2-VP conferred a PZC of basic character. Through adsorption isotherms, it was determined  that there is a higher adsorption capacity of the MIPs at acidic pH following a pseudo-second-order kinetic model. Finally, the MIPs were used to determine the non-steroidal anti-inflammatory drugs (NSAIDs) understudy in San Luis Potosí, México, wastewater, finding concentrations of 0.642, 0.985, and 0.403 mg L-1 for DCF, NPX, and IBP, respectively.

Efficient fluoride removal using Al-Cu oxide nanoparticles supported on steel slag industrial waste solid.

A SSW/Al-Cu formed from an industrial solid waste and Al-Cu Nps are utilized for the removal of fluoride from aqueous solutions. The SSW/Al-Cu was obtained by a chemical reduction method. The SSW/Al-Cu was characterized by TEM, SEM, FT-IR, XRD, BET, and pHzpc techniques. The Nps were formed as bimetallic oxides and deposited in the form of spheroidal particles forming agglomerations. The sizes of these particles range from 1 to 3 nm. The surface area and average pore width of SSW/Al-Cu were 2.99 m2/g and 17.09 nm, respectively. The adsorption kinetics were better described using the second-order model, pointing to chemical adsorption with an equilibrium time of 540 min. The thermodynamic parameters obtained here confirm the spontaneous and endothermic nature of the process. The percentage of fluoride removal was 89.5% using the four-bladed disk turbine, and computational fluid dynamics (CFD) modeling demonstrated that using the four-bladed disk turbine helped improve the fluoride removal process. The maximum adsorption capacity was 3.99 mg/g. The Langmuir-Freundlich model best describes the adsorption process, which occurred by a combination of mechanisms, such as electrostatic interactions between the ions involved in the process. This study proves that the chemical modification of this waste solid created an efficient bimetallic nanomaterial for fluoride removal. Furthermore, the method of preparation of these nanocomposites is quite scalable.