ABSTRACT
Multi-wall carbon nanotube (MWCNT) coatings are gaining increasing interest because of their special properties used in many science fields. The titania coatings are known for their improvement of osteoblast adhesion, thus changing the surface architecture. Bi-layer coatings comprising 0.25 wt% of the MWCNTs and 0.30 wt% of titania (anatase structure) were synthesized in a two-stage procedure using the electrophoretic deposition method (EPD). The MWCNT and TiO2 coatings were deposited with voltage and time parameters, respectively, of 20 V and 0.5 min, and 50 V and 4 min. EDS, AFM, SEM, Raman spectroscopy, nano-scratch test, potentiodynamic corrosion tests, wettability studies, and cytotoxicity determined with MTT (3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide) test on human dermal fibroblasts (HDF) and mouse osteoblast precursors (MC3T3), and lactate dehydrogenase (LDH) activity test were carried out on examined surfaces. The prepared MWCNT/TiO2 coating is uniformly distributed by MWCNTs and agglomerated by TiO2 particles of size ranging from 0.1 to 3 µm. Raman spectroscopy confirmed the anatase structure of the TiO2 addition and showed typical peaks of the MWCNTs. The MWCNT/TiO2 coating had higher roughness, higher adhesion strength, and improved corrosion resistance compared to the MWCNT basic coating. The results of biological tests proved that physicochemical properties of the surface, such as high porosity and wettability of MWCNT/TiO2-coated material, would support cell adhesion, but toxic species could be released to the culture medium, thus resulting in a decrease in proliferation.
ABSTRACT
Titanium implants are commonly used because of several advantages, but their surface modification is necessary to enhance bioactivity. Recently, their surface coatings were developed to induce local antibacterial properties. The aim of this research was to investigate and compare mechanical properties of three coatings: multi-wall carbon nanotubes (MWCNTs), bi-layer composed of an inner MWCNTs layer and an outer TiO2 layer, and dispersion coatings comprised of simultaneously deposited MWCNTs and nanoCu, each electrophoretically deposited on the Ti13Nb13Zr alloy. Optical microscopy, scanning electron microscopy, X-ray electron diffraction spectroscopy, and nanoindentation technique were applied to study topography, chemical composition, hardness, plastic and elastic properties. The results demonstrate that the addition of nanocopper or titanium dioxide to MWCNTs coating increases hardness, lowers Young's modulus, improves plastic and elastic properties, wear resistance under deflection, and plastic deformation resistance. The results can be attributed to different properties, structure and geometry of applied particles, various deposition techniques, and the possible appearance of porous structures. These innovative coatings of simultaneously high strength and elasticity are promising to apply for deposition on long-term titanium implants.