ABSTRACT
Studying the oxygen reduction reaction (ORR) in the alkaline electrolyte has proven to promote better catalytic responses and accessibility to commercialization. Ni-nanowires (NWs) were synthesized via the solvothermal method and modified with Pt using the spontaneous galvanic displacement method to obtain PtNi-NWs. Carbon Vulcan XC-72R (V) was used as the catalyst support, and they were doped with NH3 to obtain PtNi-NWs/V and PtNi-NWs/V-NH3. Their electrocatalytic response for the ORR was tested and PtNi-NWs/V provided the highest specific activity with logarithmic values of 0.707 and 1.01 (mA/cm2 Pt) at 0.90 and 0.85 V versus reversible hydrogen electrode (RHE), respectively. PtNi-NWs showed the highest half-wave potential (E 1/2 = 0.89 V) at 1600 rpm and 12 µgPt/cm2 in 0.1 M KOH at 25.00 ± 0.01 °C. Additionally, the catalysts followed a four-electron pathway according to the Koutecký-Levich analysis. Moreover, durability experiments demonstrated that the PtNi-NW/V performance loss was like that of commercial Pt/V along 10,000 cycles. Electrochemical ORR in situ X-ray absorption spectroscopy results showed that the Pt L3 edge white line in the PtNi-NW catalysts changed while the electrochemical potential was lowered to negatives values, from 1.0 to 0.3 V versus RHE. The Pt/O region in the in situ Fourier transforms remained the same as the potentials were applied, suggesting an alloy formation between Pt and Ni, and Pt/Pt contracted in the presence of Ni. These results provide a better understanding of PtNi-NWs in alkaline electrolytes, suggesting that they are active catalysts for ORR and can be tuned for fuel cell studies.
ABSTRACT
We report a comprehensive quantitative study of the production of refined bio-crudes via a controlled hydrothermal liquefaction (HTL) process using Ulva fasciata macroalgae (UFMA) as biomass and ultrananocrystalline Fe3O4 (UNCFO) as catalyst. X-ray diffraction and electron microscopy were applied to elucidate the formation of the high-quality nanocatalysts. Gas chromatography-mass spectroscopy (GC-MS) and CHNS analyses showed that the bio-crude yield and carbon/oxygen ratios increase as the amount of UNCFO increases, reaching a peak value of 32% at 1.25 wt% (a 9% increase when compared to the catalyst-free yield). The bio-crude is mainly composed of fatty acids, alcohols, ketones, phenol and benzene derivatives, and hydrocarbons. Their relative abundance changes as a function of catalyst concentration. FTIR spectroscopy and vibrating sample magnetometry revealed that the as-produced bio-crudes are free of iron species, which accumulate in the generated bio-chars. Our findings also indicate that the energy recovery values via the HTL process are sensitive to the catalyst loading, with a threshold loading of 1.25 wt%. GC-MS studies show that the UNCFO not only influences the chemical nature of the resulting bio-crudes and bio-chars, but also the amount of fixed carbons in the solid residues. The detailed molecular characterization of the bio-crudes and bio-chars catalyzed by UNCFO represents the first systematic study reported using UFMA. This study brings forth new avenues to advance the highly-pure bio-crude production employing active, heterogeneous catalyst materials that are recoverable and recyclable for continuous thermochemical reactions.