Adsorption behavior of methacryloyloxydecyl dihydrogen phosphate on an apatite surface at neutral pH.

This study aimed to quantify the adsorption affinity of neutralized 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP-N) toward hydroxyapatite (HA) and dicalcium phosphate dihydrate (DCPD) at pH 7.0 by employing the Langmuir isotherm model. Furthermore, the effects of inorganic phosphate (Pi) and fluoride (F(-) ) ions on the adsorption of 10-MDP-N onto HA and DCPD were examined. Fixed amounts of HA and DCPD powders were suspended in different concentrations of 10-MDP-N solutions and were incubated for 18 h. Equilibrated concentrations of 10-MDP-N were measured by spectrophotometry and the adsorption affinity was estimated using the Langmuir model. Moreover, the adsorption was examined by zeta-potential analysis. The results indicated that significant Langmuir correlation was noted in both substrates, along with an increasing negative zeta-potential; however, in DCPD the correlation was less strong. The addition of 1.0 mM Pi slightly delayed the adsorption of 10-MDP-N onto both substrates, whereas 3.0 mM Pi drastically delayed adsorption onto HA but completely inhibited adsorption onto DCPD. Up to 50 ppm, F(-) enhanced the adsorption onto HA, and the adsorption plateaued at higher concentrations of F(-) , whereas no obvious influence of F(-) on the adsorption onto DCPD was noted.

Inhibition of hydroxyapatite growth by casein, a potential salivary phosphoprotein homologue.

Salivary phosphoproteins are essential in tooth mineral regulation but are often overlooked in vitro. This study aimed to evaluate the effect of casein, as a salivary phosphoprotein homologue, on the deposition and growth of hydroxyapatite (HA) on tooth surfaces. Hydroxyapatite growth was quantified using seeded crystal systems. Artificial saliva (AS) containing HA powder and 0, 10, 20, 50, or 100 µg ml(-1) of casein, or 100 µg ml(-1) of dephosphorylated casein (Dcasein), was incubated for 0-8 h at 37°C, pH 7.2. Calcium concentrations were measured using atomic absorption spectroscopy (AAS). Surface precipitation of HA on bovine enamel and dentine blocks, incubated in similar conditions for 7 d, was examined using field emission scanning electron microscopy (FE-SEM) and transmission electron microscopy (TEM) with selected area electron diffraction (SAED). Casein adsorption was assessed using modified Lowry assays and zeta-potential measurements. The AAS results revealed a concentration-dependent inhibition of calcium consumption. Hydroxyapatite precipitation occurred when no casein was present, whereas precipitation of HA was apparently completely inhibited in casein-containing groups. Adsorption data demonstrated increasingly negative zeta-potential with increased casein concentration and an affinity constant similar to proline-rich proteins with Langmuir modelling. Casein inhibited the deposition and growth of HA primarily through the binding of esterized phosphate to HA active sites, indicating its potential as a mineral-regulating salivary phosphoprotein homologue in vitro.