Carbon-Fiber-Recycling Strategies: A Secondary Waste Stream Used for PA6,6 Thermoplastic Composite Applications.

With a view to achieving sustainable development and a circular economy, this work focused on the possibility to valorize a secondary waste stream of recycled carbon fiber (rCF) to produce a 3D printing usable material with a PA6,6 polymer matrix. The reinforcing fibers implemented in the research are the result of a double-recovery action: starting with pyrolysis, long fibers are obtained, which are used to produce non-woven fabrics, and subsequently, fiber agglomerate wastes obtained from this last process are ground in a ball mill. The effect of different amounts of reinforcement at 5% and 10% by weight on the mechanical properties of 3D-printed thermoplastic composites was investigated. Although the recycled fraction was successfully integrated in the production of filaments for 3D printing and therefore in the production of specimens via the fused deposition modeling technique, the results showed that fibers did not improve the mechanical properties as expected, due to an unsuitable average size distribution and the presence of a predominant dusty fraction ascribed to the non-optimized ball milling process. PA6,6 + 10 wt.% rCF composites exhibited a tensile strength of 59.53 MPa and a tensile modulus of 2.24 GPa, which correspond to an improvement in mechanical behavior of 5% and 21% compared to the neat PA6,6 specimens, respectively. The printed composite specimens loaded with the lowest content of rCF provided the greatest improvement in strength (+9% over the neat sample). Next, a prediction of the "optimum" critical length of carbon fibers was proposed that could be used for future optimization of recycled fiber processing.

Different Production Processes for Thermoplastic Composite Materials: Sustainability versus Mechanical Properties and Processes Parameter.

Up to now, fiber-reinforced composites with thermoplastic matrix have seen limited fields of use in the structural scope due to their high viscosity in the molten state, which results in poor impregnability of the reinforcement, leading to mechanical properties of the finished product that are not comparable to those of thermosets. Although the latter still dominate the various sectors of automotive, aerospace, transportation and construction, new applications involving the production of thermoplastic composites are growing rapidly, offering new approaches to the solution of this problem. The aim of this work is to study and evaluate the state of the art on the manufacturing processes of thermoplastic matrix composite, analyzing the parameters that come into play and that most influence the process and material performance. The advantages of film stacking and powder impregnation techniques are contrasted by the versatility of hybrid fabrics and, at the same time, parameters such as pressure and temperature must be carefully considered. A description of different thermoplastic composite processes such as powder impregnation, film stacking molding, hybrid woven fabric, hybrid yarn and products follows, which represent the current possibilities to move from a thermosetting matrix composite to a thermoplastic one, upon which the concept of sustainability is based. This article wants to present an overview of research that has been done in manufacturing thermoplastic reinforced composites and will serve as a baseline and aid for further research and development efforts.