A new series of magnetic and luminescent layered hybrid materials obtained from thianthrene phosphonic acid: M(H2O)PO3-S2C12H7 (M = Cu, Zn) and M(H2O)2(PO2OH-S2C12H7)2 (M = Mn, Co).

Four new metallophosphonates with the chemical formulae M(H2O)PO3-S2C12H7 (M = Cu, Zn) and M(H2O)2(PO2OH-S2C12H7)2 (M = Mn, Co) were synthesized using a hydrothermal route from the original bent rigid thianthrene-2-ylphosphonic acid (TPA). This organic precursor crystallizes in a non-centrosymmetric space group P212121 and presents a unique bent geometry due to the presence of two sulfur atoms in its rigid platform architecture. Obtained as single crystal and polycrystalline powders, the structures of the four hybrid materials were solved using X-ray diffraction on single crystals in a monoclinic P21/c space group. These compounds adopt a lamellar structure consisting of one inorganic subnetwork alternating with a 'sawtooth' double organic -S2C12H7 subnetwork. The inorganic layers of these compounds are made of (PO3C) or partially deprotonated (PO2OHC) tetrahedra connected by the apices to isolated ZnO3(H2O) tetrahedra, Cu2O6(H2O)2 copper dimers and cobalt and manganese MO4(H2O)2 octahedra, where the latter two exhibit an isotype structure. Thermogravimetric analysis was performed to confirm the amount of water molecules present in the formula, to track the dehydration process of the structures, and to evaluate their thermal stability. The magnetic properties of the copper, cobalt, and manganese-based materials were investigated from 2 K to 300 K by using a SQUID magnetometer revealing dominant antiferromagnetic interactions with Weiss temperatures of -8.0, -10, and -1 K, respectively. These magnetic behaviors were further corroborated by first-principles simulations based on Density Functional Theory (DFT). Finally, the absorption and photoluminescence properties of both the ligand and hybrid materials were investigated, revealing diverse excitation and recombination mechanisms. The organic moiety based on thianthrene significantly influenced the absorption and emission, with additional peaks attributed to transition metals. Singlet and triplet states recombination were observed, accompanied by an unidentified quenching mechanism affecting the triplet state lifetime.

M(H2O)(PO3C10H6OH)·(H2O)0.5 (M = Co, Mn, Zn, Cu): a new series of layered metallophosphonate compounds obtained from 6-hydroxy-2-naphthylphosphonic acid.

Four new metallophosphonates M(H2O)(PO3C10H6OH)·(H2O)0.5 (M = Mn, Co, Cu, Zn) were obtained as single crystal and polycrystalline powders by hydrothermal synthesis from the precursors 6-hydroxy-2-naphthylphosphonic acid and the corresponding metal salts. These analogous hybrids crystalized in the space group P121/c1 in a lamellar structure. Their layered structures consisted of inorganic [M(H2O)(PO3C)] layers stacked with organic bilayers of 6-hydroxy-2-naphthyl moieties "HO-C10H6" and free water molecules. Their structures were determined by single crystal X-ray diffraction and confirmed by powder X-ray diffraction and Le Bail refinement for the powder sample. The removal of water upon heating at 250 °C was studied by thermogravimetric analysis and temperature-dependent powder X-ray diffraction. Their magnetic properties were studied by SQUID magnetometry and show antiferromagnetic behavior for the Co analogue and the occurrence of a canted antiferromagnetic order at TN = 12.2 K for the Mn analogue. The Cu compound displayed an unprecedented ferromagnetic behavior. Their absorption and luminescence properties were investigated and revealed that the ligand and the compounds displayed a common behavior below a wavelength of 400 nm. Specific absorption bands were found in the compounds with Co2+ and Cu2+ at 539 nm and 849 nm, respectively. Moreover, particular luminescence bands were found for the compounds with Mn2+, Co2+ and Zn2+ at 598 nm, 551 nm and 530 and 611 nm, respectively.

Silver-based hybrid materials from meta- or para-phosphonobenzoic acid: influence of the topology on silver release in water.

Three novel silver-based metal-organic frameworks materials, which were synthesized from either 3-phosphono or 4-phosphonobenzoic acid and silver nitrate, are reported. The novel hybrids were synthesized under hydrothermal conditions; the pH of the reaction media was controlled by adding different quantities of urea thereby producing different topologies. Compound 1 (Ag3(4-PO3-C6H4-COO)), synthesized in the presence of urea, exhibits a compact 3D structure in which both phosphonic acid and carboxylic acid functional groups are linked to the silver-based inorganic network. Compound 2 (Ag(4-PO3H-C6H4-COOH)), which was synthesized at lower pH (without urea), has a layered structure in which only the phosphonic acid functional groups from 4-phosphonobenzoic acid moieties are linked to the silver inorganic network; the carboxylic acid groups being engaged in hydrogen bonds. Finally, material 3 (Ag(3-PO3H-C6H4-COOH)) was synthesized from 3-phosphonobenzoic acid and silver nitrate without urea. This material 3 features a layered structure exhibiting carboxylic acid functional groups linked via hydrogen bonds in the interlayer space. After the full characterization of these materials (single X-ray structure, IR, TGA), their ability to release silver salts in aqueous environment was measured. Silver release, determined in aqueous solution by cathodic stripping voltammetry, shows that the silver release capacity of these materials is dependent on the topology of the hybrids. The more compact structure 1 is extremely stable in water with only trace levels of silver ions being detected. On the other hand, compounds 2 and 3, in which only the phosphonic acid functional groups were bonded to the inorganic network, released larger quantities of silver ions into aqueous solution. These results which were compared with the silver release of the previously described compound 4 (Ag6(3-PO3-C6H4-COO)2). The results clearly show that the release capacity of silver-based metal organic framework can be tuned by modifying their topology which, in the present study, is governed by the regio-isomer of the organic precursor and the synthetic conditions under which the hybrids are prepared.

Structural study of hydrated/dehydrated manganese thiophene-2,5-diphosphonate metal organic frameworks, Mn2(O3P-C4H2S-PO3)·2H2O.

Synthesis of thiophene-2,5-diphosphonic acid 2 is reported, and its use for synthesis of the original pristine materials Mn(2)(O(3)P-C(4)H(2)S-PO(3))·2H(2)O 3 is reported. The structure of material 3 has been fully resolved from single-crystal X-ray diffraction. Mn(2)(O(3)P-C(4)H(2)S-PO(3))·2H(2)O 3 crystallizes in a monoclinic cell (space group P2) with the following parameters: a = 11.60(1) Å, b = 4.943(5) Å, c = 19.614(13) Å, ß = 107.22°. A noticeable feature of the structure of compound 3 is the orientation of the thiophene heterocycles that adopt two different orientations in two successive layers (along c). Thermal analysis of compound 3 indicates that the water molecules are easily removed from 160 to 230 °C while the dehydrated structure is stable up to 500 °C. The dehydrated compound obtained from 3 can be rehydrated to give the polymorphic compound Mn(2)(O(3)P-C(4)H(2)S-PO(3))·2H(2)O 4, which crystallizes in an orthorhombic cell (space group Pnam) with the following parameters: a = 7.5359(3) Å, b = 7.5524(3) Å, c = 18.3050(9) Å. The main difference between the structures of 3 and 4 arises from both the orientation of the thiophene rings (herringbone-type organization in 4) and the structure of the inorganic layers. The thiophene-2,5-diphosphonic acid moieties engaged in materials 3 and 4 adopt a different orientation likely due to rotation around the P-C bonds and via the dehydrated state 5, which is likely more flexible than the hydrated states. Study of the magnetic properties performed on compound 3 and 4 and on the dehydrated compounds Mn(2)(O(3)P-C(4)H(2)S-PO(3)) 5 complemented by the structural study has permitted us to characterize the antiferromagnetic ground state of sample 3, a weak ferromagnetic component in sample 4, and complete paramagnetic behavior in sample 5.

The dehydration of SrTeO3(H2O)--a topotactic reaction for preparation of the new metastable strontium oxotellurate(IV) phase ε-SrTeO3.

Microcrystalline single-phase strontium oxotellurate(IV) monohydrate, SrTeO(3)(H(2)O), was obtained by microwave-assisted hydrothermal synthesis under alkaline conditions at 180 °C for 30 min. A temperature of 220 °C and longer reaction times led to single crystal growth of this material. The crystal structure of SrTeO(3)(H(2)O) was determined from single crystal X-ray diffraction data: P2(1)/c, Z = 4, a = 7.7669(5), b = 7.1739(4), c = 8.3311(5) Å, ß = 107.210(1)°, V = 443.42(5) Å(3), 1403 structure factors, 63 parameters, R[F(2)>2σ(F(2))] = 0.0208, wR(F(2) all) = 0.0516, S = 1.031. SrTeO(3)(H(2)O) is isotypic with the homologous BaTeO(3)(H(2)O) and is characterised by a layered assembly parallel to (100) of edge-sharing [SrO(6)(H(2)O)] polyhedra capped on each side of the layer by trigonal-prismatic [TeO(3)] units. The cohesion of the structure is accomplished by moderate O-H···O hydrogen bonding interactions between donor water molecules and acceptor O atoms of adjacent layers. In a topochemical reaction, SrTeO(3)(H(2)O) condensates above 150 °C to the metastable phase ε-SrTeO(3) and transforms upon further heating to δ-SrTeO(3). The crystal structure of ε-SrTeO(3), the fifth known polymorph of this composition, was determined from combined electron microscopy and laboratory X-ray powder diffraction studies: P2(1)/c, Z = 4, a = 6.7759(1), b = 7.2188(1), c = 8.6773(2) Å, ß = 126.4980(7)°, V = 341.20(18) Å(3), R(Fobs) = 0.0166, R(Bobs) = 0.0318, Rwp = 0.0733, Goof = 1.38. The structure of ε-SrTeO(3) shows the same basic set-up as SrTeO(3)(H(2)O), but the layered arrangement of the hydrous phase transforms into a framework structure after elimination of water. The structural studies of SrTeO(3)(H(2)O) and ε-SrTeO(3) are complemented by thermal analysis and vibrational spectroscopic measurements.

Remarkable thermal stability of Eu(4-phosphonobenzoate): structure investigations and luminescence properties.

A new 3D rare-earth hybrid material Eu(p-O(3)PC(6)H(4)COO) has been synthesised by a hydrothermal route from Eu(NO(3))(3) x 5 H(2)O and the rigid precursor, 4-phosphonobenzoic acid. The structure of Eu(p-O(3)PC(6)H(4)COO) has been solved by X-ray diffraction on a powder sample and is described as an inorganic network in which both carboxylic and phosphonic acid groups are linked to Eu ions forming a three-dimensional architecture. Thermal analysis performed on this compound has underlined its remarkable stability up to 510 degrees C and an optical study has been conducted to examine its luminescence properties that have been related to the structure of the material. The structural and luminescence properties have also been compared with the related material Eu phenylphosphonate.

Pyrazolino[60]fullerene-oligophenylenevinylene dumbbell-shaped arrays: synthesis, electrochemistry, photophysics, and self-assembly on surfaces.

Symmetrically substituted oligophenylenevinylene (OPV) derivatives bearing terminal p-nitrophenylhydrazone groups have been prepared and used for the synthesis of dumbbell-shaped bis(pyrazolino[60]fullerene)-OPV systems. In these triad arrays, the OPV-type fluorescence is dramatically quenched as a consequence of ultrafast OPV-->C60 singlet energy transfer. In its turn the fullerene singlet state is quenched by pyrazoline-->C60 electron transfer, in line with the behavior of the corresponding reference fullerene molecule. The occurrence of electron transfer in the multicomponent arrays is evidenced by recovery of fullerene fluorescence at 77 K in CH2Cl2 and in toluene at 298 K. Under these conditions the OPV-->C60 energy transfer is unaffected. The rate of this process turns out to be higher for the OPV trimer than for the corresponding pentameric OPV arrays, in agreement with energy-transfer theory expectations. Scanning tunneling microscopy (STM) and scanning force microscopy (SFM) revealed that the bis(pyrazolino[60]fullerene)-OPV can self-assemble into ordered layered crystalline architectures on the basal plane of highly oriented pyrolitic graphite.