ABSTRACT
A novel superparamagnetic state has been observed in high quality La0.7Sr0.3MnO3 (LSMO) thin films directly grown by rf-sputtering on SiOx/Si(100) substrates. The films are nanostructured without grain boundaries, constituted by locally epitaxial nanoregions grown layer-by-layer with out-of-plane (012) preferential orientation, induced by the constrain of the native silicon oxide. Low magnetic field ZFC-FC magnetization curves show a cross-over from superparamagnetic to ferromagnetic state dependent of the thickness. The thicker film (140 nm) exhibits typical ferromagnetic order. The thinner films (40 and 60 nm) exhibit superparamagnetic behavior attributed to interacting ferromagnetic monodomain nanoregions with critical size, random in-plane oriented, where the inter-monodomain boundaries with surface spin-glass structure regulate the blocking of magnetization depending on the magnetic field intensity. M(H) hysteresis loops showed noticeable coercive fields in all samples, larger than those reported for LSMO. Such properties of half-metal LSMO film foresee potential integration in new Si-technology nanodevices in Spintronics.
ABSTRACT
In this study, bimetallic nanoparticles (BMNPs) with different mass ratios of Cu and Fe were evaluated. The influence of the morphology on the removal of pollutants was explored through theoretical and experimental studies, which revealed the best structure for removing arsenate (As(V)) in aqueous systems. To evidence the surface characteristics and differences among BMNPs with different mass proportions of Fe and Cu, several characterization techniques were used. Microscopy techniques and molecular dynamics simulations were applied to determine the differences in morphology and structure. In addition, X-ray diffraction (XRD) was used to determine the presence of various oxides. Finally, the magnetization response was evaluated, revealing differences among the materials. Our cumulative data show that BMNPs with low amounts of Cu (Fe0.9Cu0.1) had a non-uniform core-shell structure with agglomerate-type chains of magnetite, whereas a Janus-like structure was observed in BMNPs with high amounts of Cu (Fe0.5Cu0.5). However, a non-uniform core-shell structure (Fe0.9Cu0.1) facilitated electron transfer among Fe, Cu and As, which increased the adsorption rate (k), capacity (qe) and intensity (n). The mechanism of As removal was also explored in a comparative study of the phase and morphology of BMNPs pre- and post-sorption.