ABSTRACT
A novel superparamagnetic state has been observed in high quality La0.7Sr0.3MnO3 (LSMO) thin films directly grown by rf-sputtering on SiOx/Si(100) substrates. The films are nanostructured without grain boundaries, constituted by locally epitaxial nanoregions grown layer-by-layer with out-of-plane (012) preferential orientation, induced by the constrain of the native silicon oxide. Low magnetic field ZFC-FC magnetization curves show a cross-over from superparamagnetic to ferromagnetic state dependent of the thickness. The thicker film (140 nm) exhibits typical ferromagnetic order. The thinner films (40 and 60 nm) exhibit superparamagnetic behavior attributed to interacting ferromagnetic monodomain nanoregions with critical size, random in-plane oriented, where the inter-monodomain boundaries with surface spin-glass structure regulate the blocking of magnetization depending on the magnetic field intensity. M(H) hysteresis loops showed noticeable coercive fields in all samples, larger than those reported for LSMO. Such properties of half-metal LSMO film foresee potential integration in new Si-technology nanodevices in Spintronics.
ABSTRACT
The kinetics of oxygen incorporation (in-diffusion process) and excorporation (out-diffusion process), in YBa2Cu3O6+x (YBCO) epitaxial thin films prepared using the chemical solution deposition (CSD) methodology by the trifluoroacetate route, was investigated by electrical conductivity relaxation measurements. We show that the oxygenation kinetics of YBCO films is limited by the surface exchange process of oxygen molecules prior to bulk diffusion into the films. The analysis of the temperature and oxygen partial pressure influence on the oxygenation kinetics has drawn a consistent picture of the oxygen surface exchange process enabling us to define the most likely rate determining step. We have also established a strategy to accelerate the oxygenation kinetics at low temperatures based on the catalytic influence of Ag coatings thus allowing us to decrease the oxygenation temperature in the YBCO thin films.