ABSTRACT
In recent years, there has been considerable interest in the use of natural fibers as potential reinforcing fillers in polymer composites despite their hydrophilicity, which limits their widespread commercial application. The present study explored the fabrication of nanocomposites by melt mixing, using an internal mixer followed by a compression molding technique, and incorporating rice husk (RH) as a renewable natural filler, montmorillonite (MMT) nanoclay as water-resistant reinforcing nanoparticles, and polypropylene-grafted maleic anhydride (PP-g-MAH) as a compatibilizing agent. To correlate the effect of MMT delamination and MMT/RH dispersion in the composites, the mechanical and thermal properties of the composites were studied. XRD analysis revealed delamination of MMT platelets due to an increase in their interlayer spacing, and SEM micrographs indicated improved dispersion of the filler(s) from the use of compatibilizers. The mechanical properties were improved by the incorporation of MMT into the PP/RH system and the reinforcing effect was remarkable as a result of the use of compatibilizing agent. Prolonged water exposure of the prepared samples decreased their tensile and flexural properties. Interestingly, the maximum decrease was observed for PP/RH composites and the minimum was for MMT-reinforced and PP-g-MAH-compatibilized PP/RH composites. DSC results revealed an increase in crystallinity with the addition of filler(s), while the melting and crystallization temperatures remained unaltered. TGA revealed that MMT addition and its delamination in the composite systems improved the thermal stability of the developed nanocomposites. Overall, we conclude that MMT nanoclay is an effective water-resistant reinforcing nanoparticle that enhances the durability, mechanical properties, and thermal stability of composites.
ABSTRACT
The present study deals with the fabrication of epoxy composites reinforced with 50 wt% of date palm leaf sheath (G), palm tree trunk (L), fruit bunch stalk (AA), and leaf stalk (A) as filler by the hand lay-up technique. The developed composites were characterized and compared in terms of mechanical, physical and morphological properties. Mechanical tests revealed that the addition of AA improves tensile (20.60-40.12 MPa), impact strength (45.71-99.45 J/m), flexural strength (32.11-110.16 MPa) and density (1.13-1.90 g/cm3). The water absorption and thickness swelling values observed in this study were higher for AA/epoxy composite, revealing its higher cellulosic content, compared to the other composite materials. The examination of fiber pull-out, matrix cracks, and fiber dislocations in the microstructure and fractured surface morphology of the developed materials confirmed the trends for mechanical properties. Overall, from results analysis it can be concluded that reinforcing epoxy matrix with AA filler effectively improves the properties of the developed composite materials. Thus, date palm fruit bunch stalk filler might be considered as a sustainable and green promising reinforcing material similarly to other natural fibers and can be used for diverse commercial, structural, and nonstructural applications requiring high mechanical resistance.
ABSTRACT
TEMPO-oxidize nanocellulose (TONC) suspension has been obtained from total chlorine free (TCF) oil palm empty-fruit-bunches (OPEFB) pulp using 4-acetamido-TEMPO (2,2,6,6-tetramethyl piperidin-1-oxyl) mediated oxidation with sodium hypochlorite and sodium bromide in water at 25⯰C and pH 10. TONC suspension with varied content from 0.5 to 6% (w/w) reinforced polyvinyl alcohol (PVA) polymer based nanocomposite films were prepared by the casting method. The structural interaction between the TONC and PVA was characterized by the Fourier transform infrared (FT-IR) spectroscopy, nuclear magnetic resonance (NMR) spectroscopy, X-ray diffraction (XRD) and scanning electron microscopy (SEM). It was found that the 4% (w/w) TONC content reinforced nanocomposite exhibited the highest tensile strength and modulus with an increase of 122% and 291% respectively, compared to PVA while the elongation at break decreased about 42.7%. Thermal stability of PVA based nanocomposite films was improved after incorporation of TONC. Incorporation of TONC in PVA film increases its crystallinity due to strongly linking between the hydroxyl groups of materials however considerable decreases beyond 2â¯wt% loading are observed. TONC incorporation beyond 2â¯wt% also reduces the melting temperature peaks and enthalpy of nanocomposite films. FT-IR spectra, NMR and SEM indicate that there is interaction between the TONC and PVA.