ABSTRACT
Thermoplastic starch (TPS) composites with oil palm mesocarp fiber waste were prepared using compression molding. Oil palm mesocarp fiber (PC) was reduced to powder (MPC) by dry grinding in a planetary ball mill at various speeds and grinding times. It was found that fiber powder with the smallest particle size (33 µm) was obtained at a rotation speed of 200 rpm after milling for 90 min. A TPS composite with 50 wt% of MPC showed the highest tensile strength, thermal stability, and water resistance. A biodegradable seeding pot was produced from this TPS composite that was slowly degraded by microorganisms in the soil without releasing pollutants. The pot could support certain commercially and domestically grown plants for the duration of their growth period and showed potential as an innovative product that could replace existing non-biodegradable products.