ABSTRACT
In an effort to reconcile the various interpretations for the cation components of the 2p3/2observed in x-ray photoelectron spectroscopy (XPS) of several spinel oxide materials, the XPS spectra of both spinel alloy nanoparticles and crystalline thin films are compared. We observed that different components of the 2p3/2core level XPS spectra, of these inverse spinel thin films, are distinctly surface and bulk weighted, indicating surface-to-bulk core level shifts in the binding energies. Surface-to-bulk core level shifts in binding energies of Ni and Fe 2p3/2core levels of NiFe2O4thin film are observed in angle-resolved XPS. The ratio between surface-weighted components and bulk-weighted components of the Ni and Fe core levels shows appreciable dependency on photoemission angle, with respect to surface normal. XPS showed that the ferrite nanoparticles NixCo1-xFe2O4(x= 0.2, 0.5, 0.8, 1) resemble the surface of the NiFe2O4thin film. Surface-to-bulk core level shifts are also observed in CoFe2O4and NiCo2O4thin films but not as significantly as in NiFe2O4thin film. Estimates of surface stoichiometry of some spinel oxide nanoparticles and thin films suggested that the apportionment between cationic species present could be farther from expectations for thin films as compared to what is seen with nanoparticles.
ABSTRACT
Ferro-piezoceramic materials (FPCM) with different degrees of ferrohardness were fabricated by double solid-phase synthesis followed by the sintering technique using hot pressing method. The X-ray studies carried out in a wide temperature range showed that with increasing temperature, each of the studied FPCM undergoes a series of phase transformations, accompanied by a change in the symmetry of the unit cell. In this case, near the phase transition to the nonpolar cubic phase, in each of the FPCM, the formation of a fuzzy symmetry region is observed, which is characterized by weak distortions and temperature-time instability of the crystal structure. The study of the piezoelectric modulus d33 in the quasi-static regime as a function of temperature made it possible to reveal the different nature of its behavior in materials of various degrees of ferrohardness. It was shown that the conservation of the state in ferrosoft materials above the Curie temperature is associated with the relaxation nature of the change in their properties, the existence of a region of fuzzy symmetry (noncubic phase) in them above the Curie temperature, and increased inertia of the system. The expediency of taking into account the presented results in the development of electromechanical converters based on FPCM of various degrees of ferrohardness, operated under temperature effects, including cyclic ones, was shown.