ABSTRACT
Purpose: To compare the nanoleakage between bulkfill and incremental-fill resin composites in class II slot preparations for primary and permanent teeth restored by the snowplow technique. Materials and Methods: Class II slots were prepared in 32 M (16 exfoliated/extracted primary and 16 permanent molars). Optibond All-InOne self-etching adhesive was applied and cured. A flowable composite, Premise, was then injected into the gingival seat without curing using the snowplow technique. Cavities were restored using Sonicfill/bulkfill or microhybrid Herculite composites. Energy dispersive X-ray spectrometry was used to assess nanoleakage as silver deposition percentages along the axial and cervical walls. Multivariate analysis of variance was used to assess the effect of tooth type (primary and permanent teeth) and placement technique (bulkfill and incremental techniques) on nanoleakage at the axial and cervical walls. Results: Bulkfill restorations had significantly greater nanoleakage than incremental restorations at the cervical walls in primary and permanent molars (mean = 1.21 vs 0.49 in primary molars and 0.76 vs 0.24 in permanent molars). Equivalent results were observed at the axial walls of the restorations (mean = 0.66 vs 0.14 in primary molars and 0.28 vs 0.08 in permanent molars, with a P value of<0.001). Conclusions: Less nanoleakage was observed in class II slot/snowplow resin-composite restorations using the incremental technique compared to bulkfill in both dentitions. However, greater nanoleakage was detected on the cervical walls when compared with the axial walls.
ABSTRACT
Recaldent is a product of casein phosphopeptide-amorphous calcium phosphate (CPP-ACP). The remineralizing potential of CPP-ACP per se, or when combined with 0.22% Fl gel on artificially demineralized enamel using laser florescence, is investigated. Mesial surfaces of 15 sound human molars are tested using a He-Cd laser beam at 441.5 nm with 18-mW power as an excitation source on a suitable setup based on a Spex 750-M monochromator provided with a photomultiplier tube (PMT) for detection of collected autofluorescence from sound enamel. Mesial surfaces are subjected to demineralization for ten days. The spectra from demineralized enamel are measured. Teeth are divided into three groups according to the remineralizing regimen: group 1 Recaldent per se, group 2 Recaldent combined with fluoride gel and ACP, and group 3 artificial saliva as a positive control. After following these protocols for three weeks, the spectra from the remineralized enamel are measured. The spectra of enamel autofluorescence are recorded and normalized to peak intensity at about 540 nm to compare spectra from sound, demineralized, and remineralized enamel surfaces. A slight red shift occurred in spectra from demineralized enamel, while a blue shift may occur in remineralized enamel. Group 2 shows the highest remineralizing potential. Combining fluoride and ACP with CPP-ACP can give a synergistic effect on enamel remineralization.