Optimization of Printing Process Variables and the Effect of Post-Heat Treatments on the Mechanical Properties of Extruded Polylactic Acid-Aluminum Composites.

Polymer extrusions are employed in the fabrication of crucial parts for automotive, aerospace, and other mechanical applications. The use of fillers and microfibers is contributing to the advancement of material extrusion polymers. In order to enhance their mechanical characteristics, printed materials undergo a post-heating process utilizing microwaves. Specimens were fabricated using polylactic acid filaments containing 2 wt% aluminum. Two sets of specimens were fabricated and subjected to testing in order to evaluate the features of extruded specimens and specimens that underwent post-heating. In terms of mechanical performance, specimens subjected to post-heating exhibited superior results compared to specimens merely subjected to extrusion. The tensile, flexural, and Shore D hardness properties of the specimens exhibited improvements of 5.07, 6.16, and 1.32%, respectively, after being subjected to heating. Furthermore, the wear rate decreased by 13.58 percent. The results of the regression analysis indicate that the print angle and the air gap exhibit the greatest influence on the observed responses. The validation test outcomes exhibit a high level of concordance with the predicted findings. The mechanical and surface properties of components extruded with filler-added material are enhanced by subsequent heating.

Effect of Prosopis Juliflora Thorns on Mechanical Properties of Plastic Waste Reinforced Epoxy Composites.

Plastics are unavoidable at this times, putting our planet in danger. The Prosopis juliflora (PJ) thorns are collected, processed, and powdered. The mechanical characteristics of these powders are examined when combined with polymer composites. Pores are the main cause of moisture input, hence using powder filler materials reduces the number of pores in the composite, increasing water resistance. The composites are made by altering three parameters: waste plastic content, filler powder composition, and chemical treatment. It was discovered that the integration of thorn powder increased the wear resistance. The composites were tested in accordance with ASTM standards, and the results were optimized. Based on the results, composite specimens were created and tested for validation.