ABSTRACT
One of the challenges in critical size bone defect repairing is the use of a porous degradable scaffold with appropriate properties to the host tissue. Nowadays, the three-dimensional (3D) printing method can produce custom and personalized scaffolds and overcome the problems of traditional methods by controlling the porosity and dimensions of biomaterial scaffolds. In this study, polylactic acid/polyethylene glycol (PLA/PEG) scaffolds were prepared with different PEG percentages (0, 5, 10, 15 and 20 wt%) by fused deposition modeling (FDM) to optimize printability and achieve suitable physico-mechanical properties and also enhance cellular behavior for bone tissue engineering and actually, this study complements previous studies. Fourier transform infrared spectroscopy (FTIR), Scanning electron microscopy (SEM) and differential scanning calorimetry (DSC) were employed for chemical, morphological and thermal evaluations, respectively. It was shown that the adding of 20 wt% PEG to PLA 3D printed scaffolds reduced water contact angle (from 78.16 ± 3.27 to 60.00 ± 2.16), and increased surface wettability. The results also showed that the mechanical properties of the printed scaffolds were not significantly reduced by adding 5 and 10 wt% of PEG. The addition of PEG increased the degradability of scaffolds during immersion in phosphate buffer saline (PBS) solution for 8 weeks and PLA/PEG20 scaffold with 50.96 % had the highest rate of degradation. MTT assay showed that none of the studied scaffolds had cytotoxicity against MG-63 cells and increasing the PEG levels to 20 wt%, increased cell viability and adhesion and osteogenic differentiation. According to the obtained physical, mechanical and biological results, PLA/PEG scaffold printed by the FDM method can be an appropriate candidate for use in bone repair applications.