ABSTRACT
OBJECTIVES: The study aimed to assess the impact of diphenyliodonium hexafluorophosphate (DPI) on the physicochemical properties of experimental resin composites (ECRs) featuring reduced concentrations of camphorquinone (CQ)/amine. METHODS: Five concentrations of CQ (0.125, 0.25, 0.5, 0.75, and 1 mol%) with dimethylaminoethyl amine benzoate (EDAB) in a 1:2 mol% ratio (CQ:EDAB) were incorporated into a 50:50 mass% monomer blend of bisphenol glycidyl methacrylate (BisGMA) and triethyleneglycol dimethacrylate (TEGDMA). An additional 5 groups with the same CQ:EDAB concentrations had 0.5 mol% DPI added. Each resin group contained 60 wt% of 0.7 µm barium-alumino-silicate glass. Light transmission (n = 3), real-time degree of polymerization (n = 3), temperature change during polymerization (n = 5), polymerization shrinkage strain (n = 3), flexural strength, and modulus (n = 12), as well as water sorption and solubility (n = 5), were evaluated. Data were analyzed using two-way ANOVA and Tukey's post-hoc test (α = 0.05). RESULTS: Light transmission was reduced in groups containing 0.125 and 0.25 mol% of CQ without DPI. DPI increased temperature, degree and rate of polymerization, despite the reduction in CQ/amine concentration. Additionally, there was an increase in polymerization shrinkage strain, flexural strength and modulus, and a reduction in water sorption and solubility in ECRs with DPI, even with lower concentrations of CQ/EDAB. SIGNIFICANCE: DPI improved the assessed properties of composites across various concentrations of CQ/EDAB, showing the benefit of reducing the quantity of CQ used without compromising the properties and curing of the resin composites.
Subject(s)
Composite Resins , Materials Testing , Polyethylene Glycols , Polymerization , Polymethacrylic Acids , Terpenes , Composite Resins/chemistry , Terpenes/chemistry , Polyethylene Glycols/chemistry , Polymethacrylic Acids/chemistry , Bisphenol A-Glycidyl Methacrylate/chemistry , Surface Properties , Onium Compounds/chemistry , Polyurethanes/chemistry , Acrylic Resins , Biphenyl Compounds , Camphor/analogs & derivativesABSTRACT
OBJECTIVES: To analyze the influence of different concentrations of 10-MDP and GPDM used, combined or not, on the bonding to zirconia. METHODS: Specimens of zirconia and a resin-composite (7 mm length, 1 mm width, and 1 mm thick) were obtained. The experimental groups were obtained according to the functional monomer (10-MDP and GPDM) and the concentrations (3 %, 5 %, and 8 %). For the groups with combined 10-MDP and GPDM, the agents were used with a proportion of 50 %/50 % wt until reaching the 3 %, 5 % and 8 % concentrations. All monomers were diluted in ethanol to obtain the primers. Two control groups were established: ethanol (negative control) and a commercial reference Monobond N (positive control). The zirconia surface treatment was performed with the primer application followed by the bonding to a resin-composite sample with a light-curing resin cement. Twenty-four hours after the adhesive procedure, a microtensile test was performed and the failure pattern of each sample was analysed with a stereoscopic magnifying glass. Data were analysed by a two-way ANOVA and Dunnet test. RESULTS: All experimental primers presented a higher bond strength than the negative control (ethanol). Excepting the 8 % GPDM primer, all groups presented statistically similar bond strength compared to the positive control, with a predominance of adhesive failure. SIGNIFICANCE: 10-MDP, GPDM, and the combination of both for the concentrations tested promote an effective chemical bonding to zirconia. However, using 10-MDP and GPDM in the same primer has no synergistic effect.