ABSTRACT
OBJECTIVE: Incorporating an enhancer such as nano-titanium dioxide into antimicrobial photodynamic therapy can improve treatment outcome.This study aimed to compare the anticandidal efficacy of photodynamic therapy by erythrosine with nano-titanium dioxide (nano-TiO2) stimulated by a blue light emitting diode with three standard dental antifungal agents. MATERIALS AND METHODS: Candida albicans biofilms on acrylic resin plates were treated for 15 minutes with either nystatin, fluconazole, Polident, 220µM erythrosine + 1% (w/w) nano-TiO2 + 15 J/cm2 blue light photodynamic therapy (Ery PDT), or distilled water. For the Ery PDT group, blue light was applied for 1 minute after incubation. After 1, 3, and 6 hours, the colony forming units in log10 (log10CFU/mL) were compared. The ultrastructure of C. albicans on the acrylic resin plates treated with erythrosine + nano-TiO2 + blue light was examined using transmission electron microscopy at magnification of 30,000x. RESULTS: After 1 hour, nystatin, Polident, and Ery PDT indifferently inhibited C. albicans. At 6 hours, Ery PDT reduced the number of viable C. albicans in biofilms by 0.28log10 CFU/mL, which was equal to the effect of fluconazole and Polident. Transmission electron microscopy demonstrated that Ery PDT altered the C. albicans cell morphology by inducing cell wall/membrane rupture. CONCLUSION: Photodynamic therapy with erythrosine + nano-TiO2 + blue light at low light power density (15 J/cm2) was as effective at inhibiting C. albicans biofilm on acrylic resin as fluconazole and Polident.
ABSTRACT
OBJECTIVE: This study sought to investigate the toothbrush-dentifrice abrasion of dental sealants. MATERIALS AND METHODS: Weight loss (∆W) and depth loss (∆D) were used as abrasion indicators. Sealant samples from nine products were soaked in dentifrice slurry and abraded by using a toothbrushing machine with a brushing force of 300 g. The mean percentages of ∆W and mean values of ∆D after 24,000 and 48,000 strokes of brushing were compared by using paired t-test. A comparison of these mean values among sealant products was performed by using one-way ANOVA and multiple comparison analysis (Scheffe's test). RESULTS: Abrasive wear was observed in all sealants. Teethmate F-1 (Kuraray Noritake, Tokyo, Japan)-a fluoride-releasing unfilled sealant-exhibited the maximum abrasive wear, with ∆W and ∆D values of 1.14% ± 0.37% and 12.84 ± 4.28 µm, respectively. Delton (Dentsply Sirona, Charlotte, North Carolina, United States), a light-cured unfilled sealant, showed the minimum abrasive wear, with ∆W and ∆D values of 0.41% ± 0.09% and 2.93 ± 1.23 µm, respectively. No statistical differences were observed among unfilled sealants except when compared with Teethmate F-1. Similarly, no differences were observed when comparing among filled sealants and flowable composite. CONCLUSION: Abrasive wear occurred in all sealants after brushing with dentifrice. Almost all unfilled sealants showed less wear compared with both filled sealants and flowable composite. However, the low abrasive values of all sealants after brushing with dentifrice implied that there is no clinical significance to this finding.