A robust, melting class bulk superhydrophobic material with heat-healing and self-cleaning properties.

Superhydrophobic (SH) materials are essential for a myriad of applications such as anti-icing and self-cleaning due to their extreme water repellency. A single, robust material simultaneously possessing melt-coatability, bulk water repellency, self-cleanability, self-healability, self-refreshability, and adhesiveness has been remaining an elusive goal. We demonstrate a unique class of melt-processable, bulk SH coating by grafting long alkyl chains on silica nanoparticle surface by a facile one-step method. The well-defined nanomaterial shows SH property in the bulk and is found to heal macro-cracks on gentle heating. It retains wettability characteristics even after abrading with a sand paper. The surface regenerates SH features (due to reversible self-assembly of nano structures) quickly at ambient temperature even after cyclic water impalement, boiling water treatment and multiple finger rubbing tests. It exhibits self-cleaning properties on both fresh and cut surfaces. This kind of coating, hitherto undisclosed, is expected to be a breakthrough in the field of melt-processable SH coatings.

Electronic and steric ligand effects in the radical polymerization of vinyl acetate mediated by beta-ketoiminate complexes of cobalt(II).

Complexes Co[OC(Ph)CHC(Me)NAr](2) [Ar=Ph, 1; o,o'-C(6)H(3)Me(2) (Xyl), 2; p-C(6)H(4)CF(3), 3] are tested in the polymerization of vinyl acetate (VAc) initiated by V-70 (0.8 equiv) at 30 degrees C. Polymerization occurs without any notable induction time yielding PVAc with relatively low polydispersity, but with higher than expected M(n) values, which indicates inefficient trapping processes. The apparent polymerization rate constant varies in the order 2>1>3. Controlled polymer growth is also observed when the polymerization is conducted in the presence of a much higher V-70/1 ratio, demonstrating that this system can also function as a transfer agent in a degenerative transfer process. Competition between chain growth and catalyzed chain transfer (CCT) is also observed, the latter prevailing at higher temperatures. Comparison of these results with previous reports on bis(beta-diketonato) complexes allows a separate assessment of ligand electronic and steric effects in the ability to control polymerization.