Kaolinite/cashew gum bionanocomposite for doxazosin incorporation and its release.

Incorporation of drugs in clay minerals has been widely proposed for the controlled-release or increased solubility of drugs. In this context, a bionanocomposite based on kaolinite and cashew gum (Kln/Gum) was synthesized and characterized by X-ray diffraction (XRD), thermal analysis (TG/DTA), and Fourier transform infrared spectroscopy (FTIR). The bionanocomposite was applied to the incorporation and further release of doxazosin mesylate (DB). The influence of solution pH (1-3), adsorbent dose (20-50 mg), initial drug concentration (20.0-70.0 mg L-1), contact time (15-300 min), and temperature (25, 35, and 45 °C) were systematically evaluated. Equilibrium was reached around 60 min, with a maximum adsorption capacity of 31.5 ± 2.0 mg g-1 at a pH of 3.0 and 25 °C. Hydrogen bonding contributed to DB incorporation on the Kln/Gum. In addition, DB maximum amounts of 16.80 ± 0.58 and 77.00 ± 2.46% were released at pH values of 1.2 and 7.4, respectively. These results indicated that the Kln/Gum bionanocomposite is an effective and promising material for the incorporation/release of drugs with similar structures to DB.

Phosphated Cellulose as an Efficient Biomaterial for Aqueous Drug Ranitidine Removal.

Crystalline cellulose chemically modified through a reaction with sodium trimetaphosphate (STMP) in an acidic or basic condition yielded Cel-P4 and Cel-P10. These phosphated solids were characterized by elemental analysis, X-ray diffraction (XRD), infrared (IR) spectroscopy, scanning electron microscopy (SEM), nuclear magnetic resonance (NMR) at the solid state for phosphorus nucleus and dispersive X-ray energy. The elemental results demonstrated that the phosphorylation reaction was more efficient in the basic medium, as supported by the amount of phosphorous content. The synthesized biomaterials decreased in crystallinity in comparison to the precursor cellulose, with an increase in roughness and present two distinct phosphorus environments in the formed structure. The phosphated cellulose in an alkaline condition was applied to sorb the drug ranitidine. This process was applied in varying pH, time, temperature and concentration. The best sorption kinetic model to fit the experimental data was the pseudo-second-order with a coefficient correlation of 0.8976, and the Langmuir isotherm model was the most adjusted to the variation in concentration. The efficient drug sorption has a low dependence on temperature, with maximum values of 85.0, 82.0 mg and 85.7 mg·g-1 for Cel-P10 at 298, 308 and 318 K, respectively. The best sorption occurred at pH = 6 with a saturation time of 210 min.