ABSTRACT
OBJECTIVE: To evaluate the antimicrobial/antibiofilm and mechanical properties, and the effect on enamel demineralization of a resin-modified GIC (RMGIC) containing CHX and nano-sized sodium trimetaphosphate (TMP). METHODS: RMGIC was associated with CHX (1.25 or 2.5%) and/or TMP (7 or 14%). Antimicrobial and antibiofilm activity were assessed using agar diffusion test and evaluation of biofilm metabolism, respectively. In addition, fluoride (F) and TMP releases as well as the diametral tensile (DTS) and compressive (CS) strength were determined. The percentage of mineral loss (%SH), integrated loss of subsurface hardness (ΔKHN) and enamel F concentrations were also evaluated. RESULTS: RMGICs containing CHX associated or not with TMP presented higher inhibition zones and effect on S. mutans biofilm. A reduction on CS was observed only for RMGIC + 2.5%CHX and on DTS for RMGIC + 2.5%CHX + 14%TMP. The highest F and TMP releases and lowest %SH and ΔKHN values were detected for RMGIC + 1.25%CHX + 14%TMP and RMGIC + 2.5%CHX + 14%TMP. Higher enamel F concentrations were observed for TMP groups. CONCLUSION: 1.25%CHX and 14%TMP increased antimicrobial/antibiofilm action and the ability to prevent enamel demineralization, with minimal effect on the mechanical properties of RMGIC. CLINICAL SIGNIFICANCE: RMGIC containing CHX and TMP is an alternative material for patients at high risk for dental caries and can be indicated for low-stress regions or provisional restorations.
Subject(s)
Chlorhexidine , Dental Caries , Glass Ionomer Cements , Polyphosphates , Dental Enamel , HumansABSTRACT
OBJECTIVE: To evaluate the effect of a fluoride dentifrice containing sodium hexametaphosphate (HMP) on enamel demineralization in situ. METHODS: This double-blind and cross-over study consisted of 3 phases (7 days each) in which 12 volunteers wore intraoral appliances containing four enamel bovine blocks. Specimens were treated (3×/day) with placebo (no F or HMP), 1100ppm F (1100F) and 1100F plus HMP1% (1100F-HMP1%) toothpastes, and the cariogenic challenge was performed using a 30% sucrose solution (6×/day). Final surface hardness, the percentage of surface hardness loss (%SH), the integrated loss of subsurface hardness (ΔKHN), as well as enamel calcium (Ca), phosphorus (P) and firmly-bound fluoride (F) were determined. Also, biofilm formed on the blocks were analyzed for F, Ca, P and insoluble extracellular polysaccharide (EPS) concentrations. Data were submitted 1-way ANOVA, followed by Student-Newman-Keuls' test (p<0.05). RESULTS: 1100F-HMP1% promoted the lowest %SH and ΔKHN among all groups (p<0.001). The addition of HMP1% to 1100F did not enhance enamel F uptake, but significantly increased enamel Ca concentrations (p<0.001). Similar EPS concentrations were seen for 1100F-HMP1% and 1100F groups (p>0.05). All the groups were supersaturated with respect to HA. However, only 1100F-HMP1% group was supersaturated with respect to CaF2 (p<0.05). The ionic activities of F(-), CaF(+) and HF(0) for the 1100F-HMP1% group were the highest among all groups (p<0.001). CONCLUSION: The addition of HMP1% to a conventional toothpaste significantly reduces enamel demineralization in situ when compared to 1100F. CLINICAL RELEVANCE: This dentifrice could be a viable alternative to patients at high risk of caries.