ABSTRACT
This paper presents a study on the combined use of two by-products, namely quarry dust (QD) and ferronickel slag (FNS), as a full substitute for natural sand to improve the greenness of concrete production. Quarry dust was used in increments of 25% to a maximum of 75% substitution, where nickel slag was used as the remaining proportion of fine aggregate. All the combinations of quarry dust and nickel slag were found to be compliant with AS 2758.1 and they showed notably better grading than 100% sand. In this research, standard concrete tests, such as the slump test for fresh concrete, and compression, tensile and shrinkage tests for hardened concrete, were conducted. Scanning electron microscopy and X-ray diffraction analysis were also conducted for microstructural investigation. The results concluded that the combinations of quarry dust and nickel slag in concrete as a whole substitution of sand provide similar results for these properties. Specifically, 25% quarry dust with 75% nickel slag proved to be the most promising alternative to sand, with compressive and splitting tensile strengths of 62 and 4.29 MPa, respectively, which were 16% and 20% higher than those of the control mix. Also, lower drying shrinkage was observed for this combination compared to the control mix. The higher strength is attributed to the rough texture and angular shape of both quarry dust and nickel slag providing a better mechanical interlocking. The validity of this result has also been confirmed through image analysis of micrographs from various specimens. In microstructural investigations, specimens with QD and FNS exhibited fewer voids and a more compact surface compared to the control specimen. This shows the potential for further research into the use of quarry dust and nickel slag in the production of green concrete.
ABSTRACT
The effects of mono (single type) and hybrid (mixed types) fibres on the workability, compressive strength, flexural strength, and toughness parameters of fly ash geopolymer mortar were studied. The ratio of sand to geopolymer paste of the mortar was 2.75. It was found that workability of mortar decreased more with the use of PP fibres due to its higher dispersion into individual filaments in geopolymer mortar compared to the bundled ARG and PVA fibres. Compressive strength increased by 14% for using 1% steel with 0.5% PP fibres compared to that of the control mixture, which was 48 MPa. However, 25 to 30% decrease of compressive strength was observed in the mortars using the low-modulus fibres. Generally, flexural strength followed the trend of compressive strength. Deflection hardening behaviours in terms of the ASTM C1609 toughness indices, namely I5, I10 and I20 were exhibited by the mortars using 1% steel mono fibres, 0.5% ARG with 0.5% steel and 1% PVA with 0.5% steel hybrid fibres. The toughness indices and residual strength factors of the mortars using the other mono or hybrid fibres at 1 or 1.5% dosage were relatively low. Therefore, multiple cracking and deflection hardening behaviours could be achieved in fly ash geopolymer mortars of high sand to binder ratio by using steel fibres in mono or hybrid forms with ARG and PVA fibres.